Ferrite Toroid Core: Magnesium-Zinc Ferrite (28 : 18 : 54) Fired at 1400 °C (Snoek)
Ferrite is a ceramic magnet: iron oxide combined with other metal oxides, carrying magnetic flux while hardly conducting electricity. In his first ferrite patent (US 2,452,529, 1948) Snoek at Philips ground the oxides very fine and fired rings in oxygen. This magnesium-zinc ferrite (28 : 18 : 54 mol %) is milled 30 hours and fired 2 hours at 1400 °C; his core had an initial permeability of 150.
The picture: our diagram.
高级
3 days
说明
1
1
Mix 28 : 18 : 54 mol
Mix 28 : 18 : 54 mol
Mix pure magnesium oxide, zinc oxide and ferric oxide, 28 : 18 : 54 mol %. Ours, by weight: 10.06 g magnesium oxide, 13.06 g zinc oxide and 76.88 g ferric oxide per 100 g.
此步骤所需材料：
氧化镁10.06 克
氧化锌粉末13.06 克
氧化铁76.88 克所需工具：
等臂天平
防尘口罩2
2
Grind 30 hours in an iron ball mill
Grind 30 hours in an iron ball mill
Grind the mixture for 30 hours in an iron ball mill.
所需工具：
铁球磨机防尘口罩3
3
Mould a ring at 4 tons per cm²
Mould a ring at 4 tons per cm²
Press the powder at 4 tons per square centimetre into a ring 3 cm across with a 4 × 4 mm section.
所需工具：
液压机
环形压制模4
4
Fire 2 hours at 1400 °C, cool slowly
Fire 2 hours at 1400 °C, cool slowly
Heat the ring in oxygen for 2 hours at 1400 °C, then cool it slowly in oxygen at 5–10 °C a minute. Snoek's core: initial permeability 150.
所需工具：
管式炉
氧
高压气瓶
高温计
坩埚钳