Barium Ferrite Disc Magnet: 1 mol BaCO3 to 3.5 mol Iron Oxide, 1330 °C (Went, Philips 1956, Ex. 3)
Omegatron (Wikimedia Commons) · CC BY-SA 3.0
Charlie

Erstellt von

Charlie

28. Oktober 2026DE
2
0
0
0
0

Barium Ferrite Disc Magnet: 1 mol BaCO3 to 3.5 mol Iron Oxide, 1330 °C (Went, Philips 1956, Ex. 3)

A barium ferrite with more iron oxide: 1 mol barium carbonate to 3.5 mol, made as in Example 1 and passed through a 1330 °C furnace in 20 minutes. Went's rod held 1,600 gauss with a coercive force of 1,990 oersted. Source: J. J. Went, G. W. van Oosterhout and E. W. Gorter (Philips), US 2,762,777 (1956), Example 3. They sintered rods; discs and the magnetising are ours. Picture: ferrite magnets, Omegatron, Wikimedia Commons, CC BY-SA 3.0.
Erfahren
2 days

Anweisungen

1

Weigh barium carbonate and iron oxide

Weigh 201.1 g barium carbonate (1 mol) and 560.7 g ferric oxide (3.5 mol). Barium carbonate is poisonous if swallowed: gloves and a dust respirator.

Materialien für diesen Schritt:

Bariumcarbonat (Witherit)Bariumcarbonat (Witherit)201.1 g
Eisen(III)-oxidEisen(III)-oxid560.7 g

Benötigte Werkzeuge:

BalkenwaageBalkenwaage
GummihandschuheGummihandschuhe
P100-AtemschutzmaskeP100-Atemschutzmaske
2

Mill with alcohol 13.5 hours, dry and sieve

Grind the mixture with alcohol in a ball mill for 13.5 hours, then dry it and sieve it.

Benötigte Werkzeuge:

EisenkugelmühleEisenkugelmühle
Ethanol in Laborqualität, 95 %Ethanol in Laborqualität, 95 %
TrockenofenTrockenofen
WurfsiebWurfsieb
3

Knead with a binder and form

Mix 300 g of the powder with a binder such as polyvinyl alcohol (Went names it or nitrocellulose) into a kneadable mass. The patent extrudes rods about 3 mm across; ours: press discs at 1.5 tonnes per cm², as in its other examples. Dry them in air for about 24 hours.

Benötigte Werkzeuge:

Polyvinylalkohol-PulverPolyvinylalkohol-Pulver
Hydraulische PresseHydraulische Presse
Scheiben-PressformScheiben-Pressform
TrockenofenTrockenofen
4

Pass through a 1330 °C zone in 20 minutes

Sinter in air at 1330 °C by passing the pieces through a 10 cm hot zone at 5 mm per minute: 20 minutes in the heat.

Benötigte Werkzeuge:

RohrofenRohrofen
Hitzebeständige HandschuheHitzebeständige Handschuhe
5

Magnetise the discs

The patent gives no magnetising method. Ours: lay a disc with its faces against the poles of a strong electromagnet, switch the current on, then off. Find which face is north with a compass.

Benötigte Werkzeuge:

ElektromagnetElektromagnet
KompassKompass

Materialien

2

Benötigte Werkzeuge

14

Dieser Bauplan stellt her

Thumbnail
Platzhalter

Scheibenmagnet

Free

2
0
1

Verwandte Blueprints

Diese Blueprints teilen Wissen — Techniken, Materialien oder Prinzipien

Barium Ferrite Disc Magnet: Barium Carbonate and Iron Oxide Sintered (Went, Philips 1956)

Barium Ferrite Disc Magnet: Barium Carbonate and Iron Oxide Sintered (Went, Philips 1956)

von CharlieDE

Industriell

2
0
0
0
0
0

CC0 Gemeinfrei

Dieser Blueprint ist unter CC0 veröffentlicht. Sie dürfen dieses Werk für jeden Zweck frei kopieren, ändern, verbreiten und verwenden, ohne um Erlaubnis zu fragen.

Unterstützen Sie den Maker, indem Sie Produkte über seinen Blueprint kaufen, wo er eine Maker-Provision von Anbietern festgelegt, verdient. Oder erstellen Sie eine neue Iteration dieses Blueprints und verbinden Sie ihn in Ihrem eigenen Blueprint, um Einnahmen zu teilen.

Diskussion

(0)

Anmelden um an der Diskussion teilzunehmen

Kommentare werden geladen...