Ferrite Toroid Core: Copper-Zinc Ferrite Fired at 1050 °C, Held at 600 °C in Oxygen (Snoek)
Charlie

Erstellt von

Charlie

21. Oktober 2026DE
4
0
0
0
0

Ferrite Toroid Core: Copper-Zinc Ferrite Fired at 1050 °C, Held at 600 °C in Oxygen (Snoek)

Ferrite is a ceramic magnet: iron oxide combined with other metal oxides, carrying magnetic flux while hardly conducting electricity. Snoek at Philips (US 2,452,531, 1948) made this copper-zinc ferrite ring at a lower heat: technical copper oxide, zinc oxide and iron oxide with 1 % brownstone, fired at 1050 °C, then held 14 hours at 600 °C, all in oxygen. His ring had an initial permeability of 385. The picture: our diagram.
Erfahren
2 days

Anweisungen

1

Mix 20.7 : 31.6 : 47.7 mol + 1 % brownstone

Mix technical copper oxide, zinc oxide and iron oxide in the molecular ratio 20.7 : 31.6 : 47.7 (on the pure oxides) and add 1 % by weight of brownstone (manganese dioxide). Ours, by weight: 13.91 g copper oxide, 21.73 g zinc oxide and 64.36 g ferric oxide per 100 g, plus 1 g brownstone.

Materialien für diesen Schritt:

KupferoxidKupferoxid13.91 g
ZinkoxidpulverZinkoxidpulver21.73 g
Eisen(III)-oxidEisen(III)-oxid64.36 g
Mangandioxid (Pyrolusit)Mangandioxid (Pyrolusit)1 g

Benötigte Werkzeuge:

BalkenwaageBalkenwaage
StaubmaskeStaubmaske
2

Grind for 3 hours in an iron ball mill

Grind the mixture for 3 hours in a mill with iron balls.

Benötigte Werkzeuge:

EisenkugelmühleEisenkugelmühle
StaubmaskeStaubmaske
3

Mould a ring at 4 tons per cm²

Mould a ring 3 cm across and 4 × 4 mm in section at 4 tons per square centimetre, with water as the plastifying and binding agent.

Benötigte Werkzeuge:

Hydraulische PresseHydraulische Presse
RingpressformRingpressform
Destilliertes WasserDestilliertes Wasser
4

Fire 1 hour at 1050 °C, hold 14 hours at 600 °C

Sinter the ring in oxygen at 1050 °C for 1 hour, cool it slowly to 600 °C and hold it there for 14 hours, all in oxygen, then let it cool further. Snoek's core had an initial permeability of 385.

Benötigte Werkzeuge:

RohrofenRohrofen
SauerstoffSauerstoff
DruckgasflascheDruckgasflasche
PyrometerPyrometer
TiegelzangeTiegelzange
Hitzebeständige HandschuheHitzebeständige Handschuhe

Materialien

4

Benötigte Werkzeuge

12

Dieser Bauplan stellt her

Thumbnail
Platzhalter

Ferrit-Ringkern

Free

249
0
1

Verwandte Blueprints

Diese Blueprints teilen Wissen — Techniken, Materialien oder Prinzipien

Ferrite Toroid Core: Nickel-Zinc Ferrite Sintered at 1300 °C in Oxygen (Snoek)
Gefährlich

Ferrite Toroid Core: Nickel-Zinc Ferrite Sintered at 1300 °C in Oxygen (Snoek)

von CharlieDE

Industriell

5
0
0
0
0
0
Ferric Oxide: Hydroxide Precipitated from Ferric Chloride with Ammonia, Then Heated

Ferric Oxide: Hydroxide Precipitated from Ferric Chloride with Ammonia, Then Heated

von CharlieDE

Anorganisch

3
0
0
0
0
0
Copper(II) Oxide by Heating Copper in Air

Copper(II) Oxide by Heating Copper in Air

von CharlieDE

Chemie

17
0
0
0
0
0

CC0 Gemeinfrei

Dieser Blueprint ist unter CC0 veröffentlicht. Sie dürfen dieses Werk für jeden Zweck frei kopieren, ändern, verbreiten und verwenden, ohne um Erlaubnis zu fragen.

Unterstützen Sie den Maker, indem Sie Produkte über seinen Blueprint kaufen, wo er eine Maker-Provision von Anbietern festgelegt, verdient. Oder erstellen Sie eine neue Iteration dieses Blueprints und verbinden Sie ihn in Ihrem eigenen Blueprint, um Einnahmen zu teilen.

Diskussion

(0)

Anmelden um an der Diskussion teilzunehmen

Kommentare werden geladen...