Ferrite Toroid Core: Copper-Zinc Ferrite Sintered at 1100 °C, Presintered Twice at 900 °C (Snoek 1948, Ex. I)
A soft ferrite ring core for coils and transformers: copper, zinc and iron oxides with a little brownstone, presintered twice at 900 °C, pressed into a ring and sintered at 1100 °C in oxygen. Snoek's ring had an initial permeability of 154.
Source: J. L. Snoek, US 2,452,530 (Philips, 1948), Example I and its table. Unknown: the 'violet' iron oxide, linked to an unknown head. Picture: the patent's Fig. 4, the ring core.
Erfahren
2 days
Anweisungen
1
1
Weigh 20 : 30 : 50 mol % and 1 % brownstone
Weigh 20 : 30 : 50 mol % and 1 % brownstone
Mix 20 mol % pure copper oxide, 30 mol % pure zinc oxide and 50 mol % pure violet iron oxide, and add 1 % by weight of brownstone (manganese dioxide). Ours, by weight: 13.24 g copper oxide, 20.32 g zinc oxide and 66.44 g iron oxide per 100 g, plus 1 g brownstone. Unknown: what makes the iron oxide 'violet'; Snoek does not say.
Materialien für diesen Schritt:
Kupferoxid13.24 g
Zinkoxidpulver20.32 g
Violettes Eisenoxid66.44 g
Mangandioxid (Pyrolusit)1 gBenötigte Werkzeuge:
Balkenwaage
Staubmaske2
2
Grind half an hour in an iron ball mill
Grind half an hour in an iron ball mill
Grind the mixture for half an hour in a mill with iron balls.
Benötigte Werkzeuge:
EisenkugelmühleStaubmaske3
3
Presinter at 900 °C for 2 hours in oxygen
Presinter at 900 °C for 2 hours in oxygen
Heat the ground powder to 900 °C for 2 hours in oxygen and let it cool.
Benötigte Werkzeuge:
Rohrofen
Sauerstoff
Druckgasflasche
Pyrometer
Tiegel mit Deckel (Porzellan)
Hitzebeständige Handschuhe4
4
Grind and presinter at 900 °C again (2 of 2)
Grind and presinter at 900 °C again (2 of 2)
Grind the powder, then heat it once more to 900 °C in oxygen. Snoek gives no times for the repeats.
Benötigte Werkzeuge:
EisenkugelmühleRohrofenSauerstoffDruckgasflascheTiegel mit Deckel (Porzellan)Hitzebeständige HandschuheStaubmaske5
5
Grind 2 hours with iron balls
Grind 2 hours with iron balls
Grind it for 2 hours in a disintegrator with iron balls.
Benötigte Werkzeuge:
EisenkugelmühleStaubmaske6
6
Press a ring at 4 tons per cm²
Press a ring at 4 tons per cm²
Press the powder at 4 tons per square centimetre into a ring 3 cm across with a 4 × 4 mm cross-section.
Benötigte Werkzeuge:
Hydraulische Presse
RingpressformStaubmaske7
7
Sinter at 1100 °C in oxygen, cool 5–10 °C a minute
Sinter at 1100 °C in oxygen, cool 5–10 °C a minute
Sinter the ring at 1100 °C in a current of oxygen. Example I heats for 1 hour and cools in the oxygen at 5 to 10 °C per minute. Snoek's ring had an initial permeability of 154, measured at room temperature at 2 kHz.
Benötigte Werkzeuge:
RohrofenSauerstoffDruckgasflaschePyrometer
TiegelzangeHitzebeständige HandschuheMaterialien
4- 13.24 gPlatzhalter
- 20.32 gPlatzhalter
- 66.44 gPlatzhalter
- Platzhalter
Benötigte Werkzeuge
12- Platzhalter
- Platzhalter
- Platzhalter
- Platzhalter
- Platzhalter
- Platzhalter
- Platzhalter
- Platzhalter
- Platzhalter
- Platzhalter
- Platzhalter
- Platzhalter
Dieser Bauplan stellt her
Verwandte Blueprints
Diese Blueprints teilen Wissen — Techniken, Materialien oder Prinzipien
CC0 Gemeinfrei
Dieser Blueprint ist unter CC0 veröffentlicht. Sie dürfen dieses Werk für jeden Zweck frei kopieren, ändern, verbreiten und verwenden, ohne um Erlaubnis zu fragen.
Unterstützen Sie den Maker, indem Sie Produkte über seinen Blueprint kaufen, wo er eine Maker-Provision von Anbietern festgelegt, verdient. Oder erstellen Sie eine neue Iteration dieses Blueprints und verbinden Sie ihn in Ihrem eigenen Blueprint, um Einnahmen zu teilen.