Ferrite Toroid Core: Copper-Zinc Ferrite Sintered at 1250 °C (Snoek 1948, Ex. I)
Charlie

Erstellt von

Charlie

28. Oktober 2026DE
2
0
0
0
0

Ferrite Toroid Core: Copper-Zinc Ferrite Sintered at 1250 °C (Snoek 1948, Ex. I)

A soft ferrite ring core for coils and transformers: copper, zinc and iron oxides with a little brownstone, pressed into a ring and sintered at 1250 °C in oxygen. Snoek's ring had an initial permeability of 295. Source: J. L. Snoek, US 2,452,530 (Philips, 1948), Example I and its table. Unknown: the 'violet' iron oxide, linked to an unknown head. Picture: the patent's Fig. 4, the ring core.
Erfahren
2 days

Anweisungen

1

Weigh 20 : 30 : 50 mol % and 1 % brownstone

Mix 20 mol % pure copper oxide, 30 mol % pure zinc oxide and 50 mol % pure violet iron oxide, and add 1 % by weight of brownstone (manganese dioxide). Ours, by weight: 13.24 g copper oxide, 20.32 g zinc oxide and 66.44 g iron oxide per 100 g, plus 1 g brownstone. Unknown: what makes the iron oxide 'violet'; Snoek does not say.

Materialien für diesen Schritt:

KupferoxidKupferoxid13.24 g
ZinkoxidpulverZinkoxidpulver20.32 g
Violettes EisenoxidViolettes Eisenoxid66.44 g
Mangandioxid (Pyrolusit)Mangandioxid (Pyrolusit)1 g

Benötigte Werkzeuge:

BalkenwaageBalkenwaage
StaubmaskeStaubmaske
2

Grind half an hour in an iron ball mill

Grind the mixture for half an hour in a mill with iron balls.

Benötigte Werkzeuge:

EisenkugelmühleEisenkugelmühle
StaubmaskeStaubmaske
3

Press a ring at 4 tons per cm²

Press the powder at 4 tons per square centimetre into a ring 3 cm across with a 4 × 4 mm cross-section.

Benötigte Werkzeuge:

Hydraulische PresseHydraulische Presse
RingpressformRingpressform
StaubmaskeStaubmaske
4

Sinter at 1250 °C in oxygen, cool 5–10 °C a minute

Sinter the ring at 1250 °C in a current of oxygen. Example I heats for 1 hour and cools in the oxygen at 5 to 10 °C per minute. Snoek's ring had an initial permeability of 295, measured at room temperature at 2 kHz.

Benötigte Werkzeuge:

RohrofenRohrofen
SauerstoffSauerstoff
DruckgasflascheDruckgasflasche
PyrometerPyrometer
TiegelzangeTiegelzange
Hitzebeständige HandschuheHitzebeständige Handschuhe

Materialien

4

Benötigte Werkzeuge

11

Dieser Bauplan stellt her

Thumbnail
Platzhalter

Ferrit-Ringkern

Free

254
0
1

Verwandte Blueprints

Diese Blueprints teilen Wissen — Techniken, Materialien oder Prinzipien

Ferrite Toroid Core: Nickel-Zinc Ferrite Sintered at 1300 °C in Oxygen (Snoek)
Gefährlich

Ferrite Toroid Core: Nickel-Zinc Ferrite Sintered at 1300 °C in Oxygen (Snoek)

von CharlieDE

Industriell

15
0
0
0
0
0
Copper(II) Oxide by Heating Copper in Air

Copper(II) Oxide by Heating Copper in Air

von CharlieDE

Chemie

23
0
0
0
0
0

CC0 Gemeinfrei

Dieser Blueprint ist unter CC0 veröffentlicht. Sie dürfen dieses Werk für jeden Zweck frei kopieren, ändern, verbreiten und verwenden, ohne um Erlaubnis zu fragen.

Unterstützen Sie den Maker, indem Sie Produkte über seinen Blueprint kaufen, wo er eine Maker-Provision von Anbietern festgelegt, verdient. Oder erstellen Sie eine neue Iteration dieses Blueprints und verbinden Sie ihn in Ihrem eigenen Blueprint, um Einnahmen zu teilen.

Diskussion

(0)

Anmelden um an der Diskussion teilzunehmen

Kommentare werden geladen...