Ferrite Toroid Core: Copper-Zinc Ferrite by the Wet Process, Precipitated with Caustic Soda (Snoek 1948)
Charlie

Erstellt von

Charlie

28. Oktober 2026DE
7
0
0
0
0

Ferrite Toroid Core: Copper-Zinc Ferrite by the Wet Process, Precipitated with Caustic Soda (Snoek 1948)

Snoek's copper-zinc ferrite made the wet way: copper, zinc and iron salts thrown down together with hot caustic soda, so the particles are very fine and pure. The washed deposit is pre-heated, pressed into a ring and fired in oxygen, with a 30-hour hold at 600 °C. His core reached an initial permeability of 500. Source: J. L. Snoek, US 2,452,529 (Philips, 1948), Example II, wet process. Picture: our diagram.
Erfahren
3 days

Anweisungen

1

Dissolve the copper, zinc and iron salts

Make 1 litre of a purified solution of 0.2 mol copper sulphate, 0.3 mol zinc sulphate and 1 mol iron nitrate. Ours: 49.94 g copper sulphate pentahydrate; weigh the zinc sulphate and ferric nitrate for the hydrate you have.

Materialien für diesen Schritt:

Kupfersulfat-Pentahydrat (CuSO4·5H2O)Kupfersulfat-Pentahydrat (CuSO4·5H2O)49.94 g
ZinksulfatZinksulfat0.3 mol
Eisen(III)-nitratEisen(III)-nitrat1 mol
Destilliertes WasserDestilliertes Wasser1 l

Benötigte Werkzeuge:

BalkenwaageBalkenwaage
Becherglas aus BorosilikatBecherglas aus Borosilikat
GummihandschuheGummihandschuhe
2

Precipitate hot with 9 M caustic soda

Heat the solution and precipitate it with 0.5 litre of 9 molar caustic soda. Ours: 180 g sodium hydroxide in water to 0.5 litre. Strong alkali: goggles and gloves.

Materialien für diesen Schritt:

Natriumhydroxid — LaborqualitätNatriumhydroxid — Laborqualität180 g

Benötigte Werkzeuge:

Becherglas aus BorosilikatBecherglas aus Borosilikat
HeizplatteHeizplatte
ChemikalienschutzbrilleChemikalienschutzbrille
GummihandschuheGummihandschuhe
3

Wash, dry and pre-heat at 700 °C

Wash out the deposit, dry it, and pre-heat it at 700 °C so it moulds better.

Benötigte Werkzeuge:

FilterpapierFilterpapier
Destilliertes WasserDestilliertes Wasser
TrockenofenTrockenofen
RohrofenRohrofen
Tiegel mit Deckel (Porzellan)Tiegel mit Deckel (Porzellan)
Hitzebeständige HandschuheHitzebeständige Handschuhe
4

Mould a ring at 4 tons per cm²

Mould the powder at 4 tons per square centimetre into a ring 3 cm across with a 4 × 4 mm section.

Benötigte Werkzeuge:

Hydraulische PresseHydraulische Presse
RingpressformRingpressform
StaubmaskeStaubmaske
5

Heat 3 hours at 900 °C, cool to 600 °C, hold 30 hours

Heat the ring for about 3 hours at 900 °C, cool it to 600 °C at 5 °C per minute, hold it there for 30 hours and let it cool to room temperature, all in a current of oxygen. Snoek's core: initial permeability 500.

Benötigte Werkzeuge:

RohrofenRohrofen
SauerstoffSauerstoff
DruckgasflascheDruckgasflasche
PyrometerPyrometer
TiegelzangeTiegelzange
Hitzebeständige HandschuheHitzebeständige Handschuhe

Materialien

5

Benötigte Werkzeuge

18

Dieser Bauplan stellt her

Thumbnail
Platzhalter

Ferrit-Ringkern

Free

254
0
1

Verwandte Blueprints

Diese Blueprints teilen Wissen — Techniken, Materialien oder Prinzipien

Ferrite Toroid Core: Copper-Zinc Ferrite Milled 200 Hours, Fired at 1050 °C (Snoek)

Ferrite Toroid Core: Copper-Zinc Ferrite Milled 200 Hours, Fired at 1050 °C (Snoek)

von CharlieDE

Industriell

12
0
0
0
0
0
Ferric Nitrate: Scrap Iron Dissolved in Concentrated Nitric Acid (Thorpe 1912)
Gefährlich

Ferric Nitrate: Scrap Iron Dissolved in Concentrated Nitric Acid (Thorpe 1912)

von CharlieDE

Industriell

7
0
0
0
0
0

CC0 Gemeinfrei

Dieser Blueprint ist unter CC0 veröffentlicht. Sie dürfen dieses Werk für jeden Zweck frei kopieren, ändern, verbreiten und verwenden, ohne um Erlaubnis zu fragen.

Unterstützen Sie den Maker, indem Sie Produkte über seinen Blueprint kaufen, wo er eine Maker-Provision von Anbietern festgelegt, verdient. Oder erstellen Sie eine neue Iteration dieses Blueprints und verbinden Sie ihn in Ihrem eigenen Blueprint, um Einnahmen zu teilen.

Diskussion

(0)

Anmelden um an der Diskussion teilzunehmen

Kommentare werden geladen...