Ferrite Toroid Core: Magnesium-Zinc Ferrite (28 : 18 : 54) Fired at 1400 °C (Snoek)
Charlie

Erstellt von

Charlie

21. Oktober 2026DE
4
0
0
0
0

Ferrite Toroid Core: Magnesium-Zinc Ferrite (28 : 18 : 54) Fired at 1400 °C (Snoek)

Ferrite is a ceramic magnet: iron oxide combined with other metal oxides, carrying magnetic flux while hardly conducting electricity. In his first ferrite patent (US 2,452,529, 1948) Snoek at Philips ground the oxides very fine and fired rings in oxygen. This magnesium-zinc ferrite (28 : 18 : 54 mol %) is milled 30 hours and fired 2 hours at 1400 °C; his core had an initial permeability of 150. The picture: our diagram.
Erfahren
3 days

Anweisungen

1

Mix 28 : 18 : 54 mol

Mix pure magnesium oxide, zinc oxide and ferric oxide, 28 : 18 : 54 mol %. Ours, by weight: 10.06 g magnesium oxide, 13.06 g zinc oxide and 76.88 g ferric oxide per 100 g.

Materialien für diesen Schritt:

MagnesiumoxidMagnesiumoxid10.06 g
ZinkoxidpulverZinkoxidpulver13.06 g
Eisen(III)-oxidEisen(III)-oxid76.88 g

Benötigte Werkzeuge:

BalkenwaageBalkenwaage
StaubmaskeStaubmaske
2

Grind 30 hours in an iron ball mill

Grind the mixture for 30 hours in an iron ball mill.

Benötigte Werkzeuge:

EisenkugelmühleEisenkugelmühle
StaubmaskeStaubmaske
3

Mould a ring at 4 tons per cm²

Press the powder at 4 tons per square centimetre into a ring 3 cm across with a 4 × 4 mm section.

Benötigte Werkzeuge:

Hydraulische PresseHydraulische Presse
RingpressformRingpressform
4

Fire 2 hours at 1400 °C, cool slowly

Heat the ring in oxygen for 2 hours at 1400 °C, then cool it slowly in oxygen at 5–10 °C a minute. Snoek's core: initial permeability 150.

Benötigte Werkzeuge:

RohrofenRohrofen
SauerstoffSauerstoff
DruckgasflascheDruckgasflasche
PyrometerPyrometer
TiegelzangeTiegelzange
Hitzebeständige HandschuheHitzebeständige Handschuhe

Materialien

3

Benötigte Werkzeuge

11

Dieser Bauplan stellt her

Thumbnail
Platzhalter

Ferrit-Ringkern

Free

249
0
1

Verwandte Blueprints

Diese Blueprints teilen Wissen — Techniken, Materialien oder Prinzipien

Ferrite Toroid Core: Nickel-Zinc Ferrite Sintered at 1300 °C in Oxygen (Snoek)
Gefährlich

Ferrite Toroid Core: Nickel-Zinc Ferrite Sintered at 1300 °C in Oxygen (Snoek)

von CharlieDE

Industriell

5
0
0
0
0
0
Ferric Oxide: Hydroxide Precipitated from Ferric Chloride with Ammonia, Then Heated

Ferric Oxide: Hydroxide Precipitated from Ferric Chloride with Ammonia, Then Heated

von CharlieDE

Anorganisch

3
0
0
0
0
0

CC0 Gemeinfrei

Dieser Blueprint ist unter CC0 veröffentlicht. Sie dürfen dieses Werk für jeden Zweck frei kopieren, ändern, verbreiten und verwenden, ohne um Erlaubnis zu fragen.

Unterstützen Sie den Maker, indem Sie Produkte über seinen Blueprint kaufen, wo er eine Maker-Provision von Anbietern festgelegt, verdient. Oder erstellen Sie eine neue Iteration dieses Blueprints und verbinden Sie ihn in Ihrem eigenen Blueprint, um Einnahmen zu teilen.

Diskussion

(0)

Anmelden um an der Diskussion teilzunehmen

Kommentare werden geladen...