Neodymium Magnets: Melt-Spun Ribbon Milled, Pressed in a Field, Sintered and Magnetised at 30 kOe (Sato, Tokin, US 4,881,986)
Squirting the molten Nd-Fe-B alloy onto a spinning copper wheel freezes it into ribbon with crystals only a tenth of a micron across. Milled fine, lined up in a magnetic field, pressed and sintered, it makes a strong anisotropic magnet, which a 30 kOe pulse then magnetises.
Result: sintered neodymium magnets, above 16 MGOe when the powder is finer than 15 microns.
Source: Sato and Tachiya, US 4,881,986 (Tokin, 1989), Example 1. Not given: magnet shape and size. Picture drawn by Youblob.
Erfahren
3 days
Anweisungen
1
1
Melt the alloy in argon
Melt the alloy in argon
Weigh 35.0 % neodymium, 0.9 % boron (as ferroboron with 20 % B) and the rest electrolytic iron, by weight, and induction-melt them in argon into an ingot. Ours, worked out: 35 parts neodymium, 4.5 ferroboron, 60.5 iron. Sato's neodymium was 97 % (with Ce and Pr); ours is the 99 % metal.
Materialien für diesen Schritt:
Neodym-Metall35 parts
Ferrobor4.5 parts
Elektrolyteisen60.5 partsBenötigte Werkzeuge:
Balkenwaage
Induktionsofen
Druckgasflasche2
2
Melt-spin a ribbon
Melt-spin a ribbon
Remelt in argon and squirt the alloy through a small orifice onto a copper wheel whose rim moves at 15 m/s. It freezes into ribbon about 5 mm wide and 100 microns thick, with R2Fe14B grains about 0.1 micron.
Benötigte Werkzeuge:
Induktionsofen
SchmelzspinnanlageDruckgasflasche3
3
Ball-mill to powder
Ball-mill to powder
Crush and ball-mill the ribbon. Particle size: Sato made 0.5 to 30 microns; below 15 microns the magnet tops 16 MGOe, better below 10, best at 5 microns or less.
Benötigte Werkzeuge:
Eisenkugelmühle4
4
Press in a 20 kOe field and sinter
Press in a 20 kOe field and sinter
Press the powder at 1 ton/cm² in a 20 kOe field. Sinter at 1,050 °C for 1 hour in vacuum and 1 more hour in argon, then quench; age at 630 °C for 1 hour in argon.
Benötigte Werkzeuge:
Magnetfeldpresse
Rohrofen
VakuumpumpeDruckgasflasche5
5
Magnetise at 30 kOe
Magnetise at 30 kOe
Magnetise the sintered body in a field of about 30 kOe.
Benötigte Werkzeuge:
AufmagnetisiergerätMaterialien
3- 35 partsPlatzhalter
- 4.5 partsPlatzhalter
- 60.5 partsPlatzhalter
Benötigte Werkzeuge
9- Platzhalter
- Platzhalter
- Platzhalter
- Platzhalter
- Platzhalter
- Platzhalter
- Platzhalter
- 1 vendor sell this, none ship to you yetPlatzhalter
- Platzhalter
Dieser Bauplan stellt her
Verwandte Blueprints
Diese Blueprints teilen Wissen — Techniken, Materialien oder Prinzipien
CC0 Gemeinfrei
Dieser Blueprint ist unter CC0 veröffentlicht. Sie dürfen dieses Werk für jeden Zweck frei kopieren, ändern, verbreiten und verwenden, ohne um Erlaubnis zu fragen.
Unterstützen Sie den Maker, indem Sie Produkte über seinen Blueprint kaufen, wo er eine Maker-Provision von Anbietern festgelegt, verdient. Oder erstellen Sie eine neue Iteration dieses Blueprints und verbinden Sie ihn in Ihrem eigenen Blueprint, um Einnahmen zu teilen.