Strontium Ferrite Disc Magnet: 0.6 mol SrCO3 to 3 mol Iron Oxide, 1280 °C (Went, Philips 1956, Ex. 13)
Omegatron (Wikimedia Commons) · CC BY-SA 3.0
Charlie

Erstellt von

Charlie

28. Oktober 2026DE
2
0
0
0
0

Strontium Ferrite Disc Magnet: 0.6 mol SrCO3 to 3 mol Iron Oxide, 1280 °C (Went, Philips 1956, Ex. 13)

A strontium ferrite: 0.6 mol strontium carbonate to 3 mol iron oxide, milled, bound and formed as in Example 4, and passed through a 1280 °C furnace in 10 minutes. Went's rod held 2,100 gauss with a coercive force of 2,800 oersted. Source: J. J. Went, G. W. van Oosterhout and E. W. Gorter (Philips), US 2,762,777 (1956), Example 13. They sintered rods; discs and the magnetising are ours. Picture: ferrite magnets, Omegatron, Wikimedia Commons, CC BY-SA 3.0.
Erfahren
2 days

Anweisungen

1

Weigh strontium carbonate and iron oxide

Weigh 88.6 g strontium carbonate (0.6 mol) and 479.0 g ferric oxide (3 mol).

Materialien für diesen Schritt:

StrontiumcarbonatStrontiumcarbonat88.6 g
Eisen(III)-oxidEisen(III)-oxid479 g

Benötigte Werkzeuge:

BalkenwaageBalkenwaage
P100-AtemschutzmaskeP100-Atemschutzmaske
2

Mill with alcohol 15.5 hours, dry and sieve

As in Example 4: grind the mixture with alcohol in a ball mill for 15.5 hours, then dry it and sieve it.

Benötigte Werkzeuge:

EisenkugelmühleEisenkugelmühle
Ethanol in Laborqualität, 95 %Ethanol in Laborqualität, 95 %
TrockenofenTrockenofen
WurfsiebWurfsieb
3

Knead with a binder and form

Mix 300 g of the powder with a binder such as polyvinyl alcohol (Went names it or nitrocellulose) into a kneadable mass. The patent extrudes rods about 3 mm across; ours: press discs at 1.5 tonnes per cm², as in its other examples. Dry them in air for about 24 hours.

Benötigte Werkzeuge:

Polyvinylalkohol-PulverPolyvinylalkohol-Pulver
Hydraulische PresseHydraulische Presse
Scheiben-PressformScheiben-Pressform
TrockenofenTrockenofen
4

Pass through a 1280 °C zone in 10 minutes

Sinter in air at 1280 °C by passing the pieces through a 10 cm hot zone at 10 mm per minute: 10 minutes in the heat.

Benötigte Werkzeuge:

RohrofenRohrofen
Hitzebeständige HandschuheHitzebeständige Handschuhe
5

Magnetise the discs

The patent gives no magnetising method. Ours: lay a disc with its faces against the poles of a strong electromagnet, switch the current on, then off. Find which face is north with a compass.

Benötigte Werkzeuge:

ElektromagnetElektromagnet
KompassKompass

Materialien

2

Benötigte Werkzeuge

13

Dieser Bauplan stellt her

Thumbnail
Platzhalter

Scheibenmagnet

Free

2
0
1

Verwandte Blueprints

Diese Blueprints teilen Wissen — Techniken, Materialien oder Prinzipien

Barium Ferrite Disc Magnet: Barium Carbonate and Iron Oxide Sintered (Went, Philips 1956)

Barium Ferrite Disc Magnet: Barium Carbonate and Iron Oxide Sintered (Went, Philips 1956)

von CharlieDE

Industriell

2
0
0
0
0
0
Strontium Carbonate: Powdered Celestine Boiled with Soda Solution (Thorpe 1912)

Strontium Carbonate: Powdered Celestine Boiled with Soda Solution (Thorpe 1912)

von CharlieDE

Industriell

6
0
0
0
0
0

CC0 Gemeinfrei

Dieser Blueprint ist unter CC0 veröffentlicht. Sie dürfen dieses Werk für jeden Zweck frei kopieren, ändern, verbreiten und verwenden, ohne um Erlaubnis zu fragen.

Unterstützen Sie den Maker, indem Sie Produkte über seinen Blueprint kaufen, wo er eine Maker-Provision von Anbietern festgelegt, verdient. Oder erstellen Sie eine neue Iteration dieses Blueprints und verbinden Sie ihn in Ihrem eigenen Blueprint, um Einnahmen zu teilen.

Diskussion

(0)

Anmelden um an der Diskussion teilzunehmen

Kommentare werden geladen...