Metal Oxide Varistor: Zinc Oxide with 0.2 % Manganese Dioxide, Bismuth Oxide Paste Fired On (Masuyama 1972, Ex. 5)
A varistor with bismuth oxide fired on from a paste instead of mixed in: 99.8 % zinc oxide with 0.2 % manganese dioxide by moles, sintered at 1350 °C, coated with bismuth oxide paste and fired at 800 °C. The disc measured a C-value of 114 at 1 mA and a nonlinearity exponent n of 15.3.
Source: T. Masuyama, M. Matsuoka and T. Nishi (Matsushita), US 3,663,458 (1972), Example 5. Unknown: how the aluminium is sprayed on, what the silver paint is, and how strong the epoxy solution of the paste is. The 10 g batch is our arithmetic. Picture: the patent's drawing.
Erfahren
2 days
Anweisungen
1
1
Weigh 99.8 : 0.2 and wet-mill 5 hours
Weigh 99.8 : 0.2 and wet-mill 5 hours
Mix zinc oxide and manganese dioxide 99.8 : 0.2 by moles. Ours, for 10 g: 9.979 g zinc oxide and 0.021 g manganese dioxide (our arithmetic). Mill wet for 5 hours, then dry, as in Example 1. Unknown: the milling liquid.
Materialien für diesen Schritt:
Zinkoxidpulver9.979 g
Mangandioxid (Pyrolusit)0.021 gBenötigte Werkzeuge:
Balkenwaage
Eisenkugelmühle
Trockenofen2
2
Press discs 13 mm by 2.5 mm
Press discs 13 mm by 2.5 mm
Press discs 13 mm across and 2.5 mm thick at 340 kg/cm², as in Example 1.
Benötigte Werkzeuge:
Hydraulische Presse
Scheiben-Pressform
Messschieber3
3
Sinter 1 hour at 1350 °C and furnace-cool
Sinter 1 hour at 1350 °C and furnace-cool
As in Example 2: sinter in air at 1350 °C for 1 hour and let the discs cool in the furnace.
Benötigte Werkzeuge:
Muffelofen4
4
Lap both faces
Lap both faces
Lap both faces with silicon carbide abrasive. Example 5 gives no thickness.
Benötigte Werkzeuge:
Siliciumcarbid-KörnungMessschieber5
5
Coat with bismuth oxide paste and fire at 800 °C
Coat with bismuth oxide paste and fire at 800 °C
Coat both lapped faces with a paste of 50 % by weight bismuth oxide in a solution of epoxy resin in butyl alcohol, and fire it in air at 800 °C for 30 minutes. The bismuth oxide diffuses into the zinc oxide. Not given: how much paste, or the strength of the epoxy solution.
Materialien für diesen Schritt:
Bismutoxid1 as requiredBenötigte Werkzeuge:
Epoxidharz
n-ButanolMuffelofen6
6
Spray aluminium electrodes and attach leads
Spray aluminium electrodes and attach leads
Spray a metallised film of aluminium on both faces. Attach a lead wire to each with conductive silver paint, as in Example 1. Unknown: the spraying method and the paint.
Materialien für diesen Schritt:
Aluminiumbarren1 as required
Silberleitlack1 as required
Kupferdraht2 StückBenötigte Werkzeuge:
Unbekanntes MetallspritzverfahrenMessschieberMaterialien
6- 9.979 gPlatzhalter
- 0.021 gPlatzhalter
- 1 as requiredPlatzhalter
- 1 as requiredPlatzhalter
- 1 as requiredPlatzhalter
- 2 StückPlatzhalter
Benötigte Werkzeuge
11- Platzhalter
- Platzhalter
- Platzhalter
- Platzhalter
- Platzhalter
- Platzhalter
- Platzhalter
- Platzhalter
- Platzhalter
- Platzhalter
- Platzhalter
Dieser Bauplan stellt her
Verwandte Blueprints
Diese Blueprints teilen Wissen — Techniken, Materialien oder Prinzipien
CC0 Gemeinfrei
Dieser Blueprint ist unter CC0 veröffentlicht. Sie dürfen dieses Werk für jeden Zweck frei kopieren, ändern, verbreiten und verwenden, ohne um Erlaubnis zu fragen.
Unterstützen Sie den Maker, indem Sie Produkte über seinen Blueprint kaufen, wo er eine Maker-Provision von Anbietern festgelegt, verdient. Oder erstellen Sie eine neue Iteration dieses Blueprints und verbinden Sie ihn in Ihrem eigenen Blueprint, um Einnahmen zu teilen.