Metal Oxide Varistor: Zinc Oxide with Bismuth, Manganese and Titanium Oxides, 1350 °C (Masuyama 1972, Ex. 3)
Masuyama, Matsuoka and Nishi found that adding two more oxides to zinc oxide and bismuth oxide gives excellent non-linear properties. This is their Example 3 with manganese dioxide and titanium dioxide: 98.5 % zinc oxide and 0.5 % each of bismuth oxide, manganese dioxide and titanium dioxide by moles, sintered at 1350 °C. The disc measured a C-value of 58 at 1 mA and a nonlinearity exponent n of 12.1.
Source: T. Masuyama, M. Matsuoka and T. Nishi (Matsushita), US 3,663,458 (1972), Example 3. Unknown: how the aluminium is sprayed on and what the silver paint is. The 10 g batch is our arithmetic. Picture: the patent's drawing.
Erfahren
1 day
Anweisungen
1
1
Weigh 98.5 : 0.5 : 0.5 : 0.5 and wet-mill 5 hours
Weigh 98.5 : 0.5 : 0.5 : 0.5 and wet-mill 5 hours
Mix zinc oxide, bismuth oxide, manganese dioxide and titanium dioxide 98.5 : 0.5 : 0.5 : 0.5 by moles. Ours, for 10 g: 9.62 g zinc oxide, 0.28 g bismuth oxide, 0.052 g manganese dioxide, 0.048 g titanium dioxide (our arithmetic). Mill wet for 5 hours, then dry. Unknown: the milling liquid.
Materialien für diesen Schritt:
Zinkoxidpulver9.62 g
Bismutoxid0.28 g
Mangandioxid (Pyrolusit)0.052 g
Titandioxid0.048 gBenötigte Werkzeuge:
Balkenwaage
Eisenkugelmühle
Trockenofen2
2
Press discs 13 mm by 2.5 mm
Press discs 13 mm by 2.5 mm
Press the powder in a mould into discs 13 mm across and 2.5 mm thick at 340 kg/cm², as in Example 1.
Benötigte Werkzeuge:
Hydraulische Presse
Scheiben-Pressform
Messschieber3
3
Sinter 1 hour at 1350 °C and furnace-cool
Sinter 1 hour at 1350 °C and furnace-cool
Sinter the discs in air at 1350 °C for 1 hour, then let them cool in the furnace to room temperature (about 15-30 °C).
Benötigte Werkzeuge:
Muffelofen4
4
Lap to 10 mm by 1.5 mm
Lap to 10 mm by 1.5 mm
Lap both faces with 600-mesh silicon carbide. The finished disc is 10 mm across and 1.5 mm thick.
Benötigte Werkzeuge:
Siliciumcarbid-KörnungMessschieber5
5
Spray aluminium electrodes and attach leads
Spray aluminium electrodes and attach leads
Spray a metallised film of aluminium on both faces. Attach a lead wire to each with conductive silver paint. Unknown: the spraying method and the paint.
Materialien für diesen Schritt:
Aluminiumbarren1 as required
Silberleitlack1 as required
Kupferdraht2 StückBenötigte Werkzeuge:
Unbekanntes MetallspritzverfahrenMessschieberMaterialien
7- 9.62 gPlatzhalter
- 0.28 gPlatzhalter
- 0.052 gPlatzhalter
- 0.048 gPlatzhalter
- 1 as requiredPlatzhalter
- 1 as requiredPlatzhalter
- 2 StückPlatzhalter
Benötigte Werkzeuge
9- Platzhalter
- Platzhalter
- Platzhalter
- Platzhalter
- Platzhalter
- Platzhalter
- Platzhalter
- Platzhalter
- Platzhalter
Dieser Bauplan stellt her
Verwandte Blueprints
Diese Blueprints teilen Wissen — Techniken, Materialien oder Prinzipien
CC0 Gemeinfrei
Dieser Blueprint ist unter CC0 veröffentlicht. Sie dürfen dieses Werk für jeden Zweck frei kopieren, ändern, verbreiten und verwenden, ohne um Erlaubnis zu fragen.
Unterstützen Sie den Maker, indem Sie Produkte über seinen Blueprint kaufen, wo er eine Maker-Provision von Anbietern festgelegt, verdient. Oder erstellen Sie eine neue Iteration dieses Blueprints und verbinden Sie ihn in Ihrem eigenen Blueprint, um Einnahmen zu teilen.