Barium-Calcium Ferrite Disc Magnet: 0.09 mol BaCO3 and 0.01 mol CaCO3 (Went, Philips 1956, Ex. 19)
A ceramic magnet with a tenth of the barium replaced by calcium: 0.09 mol barium carbonate and 0.01 mol calcium carbonate to 0.6 mol iron oxide, made as in Example 18: milled, presintered at 1000 °C, milled again, formed and passed through a 1330 °C furnace in 10 minutes. Went's rod held 1,705 gauss with a coercive force of 1,110 oersted.
Source: J. J. Went, G. W. van Oosterhout and E. W. Gorter (Philips), US 2,762,777 (1956), Example 19. They sintered rods; discs and the magnetising are ours. Picture: ferrite magnets, Omegatron, Wikimedia Commons, CC BY-SA 3.0.
Avanzado
2 days
Instrucciones
1
1
Weigh barium carbonate, chalk and iron oxide
Weigh barium carbonate, chalk and iron oxide
Weigh 17.76 g barium carbonate (0.09 mol), 1.001 g calcium carbonate (0.01 mol) and 95.55 g ferric oxide (0.6 mol). Barium carbonate is poisonous if swallowed: gloves and a dust respirator.
Materiales para este paso:
Carbonato de bario (witherita)17.76 g
Carbonato de calcio (blanco de España)1.001 g
Óxido férrico95.55 gHerramientas necesarias:
Balanza de platillos
Guantes de goma
Respirador P1002
2
Mill with alcohol 4 hours, dry at 150 °C
Mill with alcohol 4 hours, dry at 150 °C
Grind with alcohol in a ball mill for 4 hours and dry in air at 150 °C.
Herramientas necesarias:
Molino de bolas de hierro
Etanol de laboratorio, 95 %
Horno de secado3
3
Presinter in air at 1000 °C for 2 hours
Presinter in air at 1000 °C for 2 hours
Fire in air at 1000 °C for 2 hours.
Herramientas necesarias:
Horno mufla
Crisol con tapa (porcelana)
Tenazas para crisol
Guantes resistentes al calor4
4
Mill again 4 hours, dry, form
Mill again 4 hours, dry, form
Grind again with alcohol for 4 hours and dry. Example 19 extrudes a rod; ours: press discs at 1.5 tonnes per cm², as Example 18 moulds its rod.
Herramientas necesarias:
Molino de bolas de hierroEtanol de laboratorio, 95 %Horno de secado
Prensa hidráulica
Matriz de prensado de discos5
5
Pass through a 1330 °C zone in 10 minutes
Pass through a 1330 °C zone in 10 minutes
Sinter at 1330 °C by passing the pieces through a 10 cm hot zone at 10 mm per minute: 10 minutes in the heat.
Herramientas necesarias:
Horno tubularGuantes resistentes al calor6
6
Magnetise the discs
Magnetise the discs
The patent gives no magnetising method. Ours: lay a disc with its faces against the poles of a strong electromagnet, switch the current on, then off. Find which face is north with a compass.
Herramientas necesarias:
Electroimán
BrújulaMateriales
3- Marcador de posición
- Marcador de posición
- 95.55 gMarcador de posición
Herramientas requeridas
15- Marcador de posición
- Marcador de posición
- Marcador de posición
- Marcador de posición
- Marcador de posición
- Marcador de posición
- Marcador de posición
- Marcador de posición
- Marcador de posición
- Marcador de posición
- Marcador de posición
- Marcador de posición
- Marcador de posición
- Marcador de posición
- Marcador de posición
Este plano hace
Blueprints relacionados
Estos blueprints comparten conocimiento — técnicas, materiales o principios
CC0 Dominio público
Este Blueprint se publica bajo CC0. Eres libre de copiar, modificar, distribuir y usar este trabajo para cualquier propósito, sin pedir permiso.
Apoya al Maker comprando productos a través de su Blueprint, donde gana una Comisión del Maker establecida por los vendedores, o crea una nueva iteración de este Blueprint e inclúyela como conexión en tu propio Blueprint para compartir ingresos.