Ferrite Toroid Core: Copper-Zinc Ferrite Fired at 1050 °C, Held at 600 °C in Oxygen (Snoek)
Ferrite is a ceramic magnet: iron oxide combined with other metal oxides, carrying magnetic flux while hardly conducting electricity. Snoek at Philips (US 2,452,531, 1948) made this copper-zinc ferrite ring at a lower heat: technical copper oxide, zinc oxide and iron oxide with 1 % brownstone, fired at 1050 °C, then held 14 hours at 600 °C, all in oxygen. His ring had an initial permeability of 385.
The picture: our diagram.
Avanzado
2 days
Instrucciones
1
1
Mix 20.7 : 31.6 : 47.7 mol + 1 % brownstone
Mix 20.7 : 31.6 : 47.7 mol + 1 % brownstone
Mix technical copper oxide, zinc oxide and iron oxide in the molecular ratio 20.7 : 31.6 : 47.7 (on the pure oxides) and add 1 % by weight of brownstone (manganese dioxide). Ours, by weight: 13.91 g copper oxide, 21.73 g zinc oxide and 64.36 g ferric oxide per 100 g, plus 1 g brownstone.
Materiales para este paso:
Óxido de cobre13.91 g
Óxido de zinc en polvo21.73 g
Óxido férrico64.36 g
Dióxido de manganeso (pirolusita)1 gHerramientas necesarias:
Balanza de platillos
Mascarilla antipolvo2
2
Grind for 3 hours in an iron ball mill
Grind for 3 hours in an iron ball mill
Grind the mixture for 3 hours in a mill with iron balls.
Herramientas necesarias:
Molino de bolas de hierroMascarilla antipolvo3
3
Mould a ring at 4 tons per cm²
Mould a ring at 4 tons per cm²
Mould a ring 3 cm across and 4 × 4 mm in section at 4 tons per square centimetre, with water as the plastifying and binding agent.
Herramientas necesarias:
Prensa hidráulica
Matriz de prensado anular
Agua destilada4
4
Fire 1 hour at 1050 °C, hold 14 hours at 600 °C
Fire 1 hour at 1050 °C, hold 14 hours at 600 °C
Sinter the ring in oxygen at 1050 °C for 1 hour, cool it slowly to 600 °C and hold it there for 14 hours, all in oxygen, then let it cool further. Snoek's core had an initial permeability of 385.
Herramientas necesarias:
Horno tubular
Oxígeno
Bombona de gas a presión
Pirómetro
Tenazas para crisol
Guantes resistentes al calorMateriales
4- 13.91 gMarcador de posición
- 21.73 gMarcador de posición
- 64.36 gMarcador de posición
- Marcador de posición
Herramientas requeridas
12- Marcador de posición
- Marcador de posición
- Marcador de posición
- Marcador de posición
- Marcador de posición
- Marcador de posición
- Marcador de posición
- Marcador de posición
- Marcador de posición
- Marcador de posición
- Marcador de posición
- Marcador de posición
Este plano hace
Blueprints relacionados
Estos blueprints comparten conocimiento — técnicas, materiales o principios
CC0 Dominio público
Este Blueprint se publica bajo CC0. Eres libre de copiar, modificar, distribuir y usar este trabajo para cualquier propósito, sin pedir permiso.
Apoya al Maker comprando productos a través de su Blueprint, donde gana una Comisión del Maker establecida por los vendedores, o crea una nueva iteración de este Blueprint e inclúyela como conexión en tu propio Blueprint para compartir ingresos.