Ferrite Toroid Core: Nickel-Zinc Ferrite Fired at 1400 °C, Held at 930 °C (Snoek)
Ferrite is a ceramic magnet: iron oxide combined with other metal oxides, carrying magnetic flux while hardly conducting electricity. In his first ferrite patent (US 2,452,529, 1948) Snoek at Philips ground the oxides very fine and fired rings in oxygen. This nickel-zinc ferrite (20 : 30 : 50 mol %) is milled 30 hours, fired 1 hour at 1400 °C and held 16 hours at 930 °C; his core had an initial permeability of 560. Nickel oxide dust is a cancer hazard: respirator on.
The picture: our diagram.
Avanzado
3 days
Contenido peligroso
Este blueprint contiene procedimientos peligrosos. Inicia sesión y habilita el contenido peligroso en la configuración de tu cuenta para ver las instrucciones paso a paso.
Iniciar sesiónEste plano hace
Blueprints relacionados
Estos blueprints comparten conocimiento — técnicas, materiales o principios
Peligroso
Ferrite Toroid Core: Nickel-Zinc Ferrite Sintered at 1300 °C in Oxygen (Snoek)
por Charlie
Industrial
5
0
0
0
0
0
Ferric Oxide: Hydroxide Precipitated from Ferric Chloride with Ammonia, Then Heated
por Charlie
Inorgánico
3
0
0
0
0
0
Peligroso
Nickel Monoxide: Nickel Hydroxide Precipitated with Alkali and Strongly Heated
por Charlie
Inorgánico
5
0
0
0
0
0
CC0 Dominio público
Este Blueprint se publica bajo CC0. Eres libre de copiar, modificar, distribuir y usar este trabajo para cualquier propósito, sin pedir permiso.
Apoya al Maker comprando productos a través de su Blueprint, donde gana una Comisión del Maker establecida por los vendedores, o crea una nueva iteración de este Blueprint e inclúyela como conexión en tu propio Blueprint para compartir ingresos.