Ferrite Toroid Core: Wet-Process Copper-Zinc Ferrite with a Stepped Anneal Down to 310 °C (Snoek 1948)
The wet-process copper-zinc ferrite ring of Snoek's Example II, given a long stepped anneal in oxygen after its 600 °C hold: 19 hours at 510 °C, 34 hours at 410 °C and 12 hours at 310 °C. The initial permeability fell from 500 to 410.
Source: J. L. Snoek, US 2,452,529 (Philips, 1948), Example II, wet process. Picture: our diagram.
Avancé
3 days
Consignes
1
1
Dissolve the copper, zinc and iron salts
Dissolve the copper, zinc and iron salts
Make 1 litre of a purified solution of 0.2 mol copper sulphate, 0.3 mol zinc sulphate and 1 mol iron nitrate. Ours: 49.94 g copper sulphate pentahydrate; weigh the zinc sulphate and ferric nitrate for the hydrate you have.
Matériaux pour cette étape :
Sulfate de cuivre pentahydraté (CuSO4·5H2O)49.94 g
Sulfate de zinc0.3 mol
Nitrate ferrique1 mol
Eau distillée1 lOutils nécessaires :
Balance à fléau
Bécher en borosilicate
Gants en caoutchouc2
2
Precipitate hot with 9 M caustic soda
Precipitate hot with 9 M caustic soda
Heat the solution and precipitate it with 0.5 litre of 9 molar caustic soda. Ours: 180 g sodium hydroxide in water to 0.5 litre. Strong alkali: goggles and gloves.
Matériaux pour cette étape :
Hydroxyde de sodium — qualité laboratoire180 gOutils nécessaires :
Bécher en borosilicate
Plaque chauffante
Lunettes-masque anti-projections chimiquesGants en caoutchouc3
3
Wash, dry and pre-heat at 700 °C
Wash, dry and pre-heat at 700 °C
Wash out the deposit, dry it, and pre-heat it at 700 °C so it moulds better.
Outils nécessaires :
Papier filtreEau distillée
Étuve de séchage
Four tubulaire
Creuset avec couvercle (porcelaine)
Gants résistants à la chaleur4
4
Mould a ring at 4 tons per cm²
Mould a ring at 4 tons per cm²
Mould the powder at 4 tons per square centimetre into a ring 3 cm across with a 4 × 4 mm section.
Outils nécessaires :
Presse hydraulique
Matrice de pressage annulaire
Masque anti-poussière5
5
Heat 3 hours at 900 °C, cool to 600 °C, hold 30 hours
Heat 3 hours at 900 °C, cool to 600 °C, hold 30 hours
Heat the ring for about 3 hours at 900 °C, cool it to 600 °C at 5 °C per minute, hold it there for 30 hours and let it cool to room temperature, all in a current of oxygen. Snoek's core: initial permeability 500.
Outils nécessaires :
Four tubulaire
Oxygène
Bouteille de gaz sous pression
Pyromètre
Pince à creusetGants résistants à la chaleur6
6
Anneal 19 h at 510 °C, 34 h at 410 °C, 12 h at 310 °C
Anneal 19 h at 510 °C, 34 h at 410 °C, 12 h at 310 °C
After the 600 °C hold, keep the core for another 19 hours at 510 °C, 34 hours at 410 °C and 12 hours at 310 °C, all in oxygen. Snoek's core: initial permeability 410.
Outils nécessaires :
Four tubulaireOxygèneBouteille de gaz sous pressionPyromètrePince à creusetGants résistants à la chaleurMatériaux
5- Espace réservé
- 0.3 molEspace réservé
- 1 molEspace réservé
- Espace réservé
- Espace réservé
Outils requis
18- Espace réservé
- Espace réservé
- Espace réservé
- Espace réservé
- Espace réservé
- Espace réservé
- Espace réservé
- Espace réservé
- Espace réservé
- Espace réservé
- Espace réservé
- Espace réservé
- Espace réservé
- Espace réservé
- Espace réservé
- Espace réservé
- Espace réservé
- Espace réservé
Ce plan fabrique
Blueprints liés
Ces blueprints partagent des connaissances — techniques, matériaux ou principes
CC0 Domaine public
Ce blueprint est publié sous CC0. Vous êtes libre de copier, modifier, distribuer et utiliser ce travail pour tout usage, sans demander la permission.
Soutenez le Maker en achetant des produits via son Blueprint où il perçoit une Commission Maker définie par les Vendeurs, ou créez une nouvelle itération de ce Blueprint et incluez-le comme connexion dans votre propre Blueprint pour partager les revenus.