Semi-Cured Phenolic Sheet: Paper Dipped in Phenol Resin and Part-Cured at 120-130 °C (Lucas, Western Electric, US 1,470,990)
Paper soaked in phenol resin is dried, then cured only part of the way, so the resin is stiff but not yet hard. Lucas did this before the final hot press so the press would not squeeze the resin out of the fibres.
Result: a dry, partly cured phenolic sheet that a later coat of phenolic resin can still bond into.
Source: Lucas, US 1,470,990 (Western Electric, 1923). Stopping before his final hot press is ours. Not given: the solvent in his resin, paper grade, mercerising strengths. Picture drawn by Youblob.
Intermédiaire
1 hour
Consignes
1
1
Dip the paper in phenol resin
Dip the paper in phenol resin
Run the paper through a bath of phenol resin of specific gravity about 0.970: about 2 minutes for plain paper, 1 minute or less if mercerised first. Ours: Liquid Bakelite as the resin; Lucas does not say how it was thinned.
Matériaux pour cette étape :
Papier1 as required
Bakélite liquide (produit de condensation phénol-formaldéhyde)1 as requiredOutils nécessaires :
Ligne d'imprégnation de préimprégné
Densimètre2
2
Optional: mercerise the paper first
Optional: mercerise the paper first
For faster, fuller soaking, first pass the paper through caustic soda, squeeze, wash in water, neutralise in an acid, wash again and dry. Strengths and the acid: not given.
Outils nécessaires :
Soude caustique (hydroxyde de sodium)Ligne d'imprégnation de préimprégné3
3
Dry at about 90 °C
Dry at about 90 °C
Dry the soaked paper in an oven at about 90 °C, just long enough to dry it.
Outils nécessaires :
Étuve de séchage4
4
Part-cure at 120-130 °C
Part-cure at 120-130 °C
Pass the dry paper through a curing oven at 120-130 °C for about 10 minutes (Lucas's description; his claim 4 says 125 °C for about 10 seconds). The resin sets as stiff as the fibres, but does not harden through.
Outils nécessaires :
Four de cuisson5
5
Dip again for 10-15 seconds and dry
Dip again for 10-15 seconds and dry
Dip the part-cured paper in phenol resin again for 10-15 seconds, then dry at about 90 °C until it can be wound on a reel. Stop here: the sheet is semi-cured. Lucas's next step, stacking and hot pressing, cures it fully.
Matériaux pour cette étape :
Bakélite liquide (produit de condensation phénol-formaldéhyde)1 as requiredOutils nécessaires :
Ligne d'imprégnation de préimprégnéÉtuve de séchageMatériaux
2- 1 as requiredEspace réservé
- Espace réservé
Outils requis
5- Espace réservé
- Espace réservé
- Espace réservé
- Espace réservé
- Espace réservé
Ce plan fabrique
Blueprints liés
Ces blueprints partagent des connaissances — techniques, matériaux ou principes
CC0 Domaine public
Ce blueprint est publié sous CC0. Vous êtes libre de copier, modifier, distribuer et utiliser ce travail pour tout usage, sans demander la permission.
Soutenez le Maker en achetant des produits via son Blueprint où il perçoit une Commission Maker définie par les Vendeurs, ou créez une nouvelle itération de ce Blueprint et incluez-le comme connexion dans votre propre Blueprint pour partager les revenus.