Carbon Resistance Strip: Carbon and Phenolic Resin in Ethyl Acetate, Cured on Semi-Cured Phenolic Sheet
Ed

Dibuat oleh

Ed

21. Oktober 2026FI
12
0
0
0
0

Carbon Resistance Strip: Carbon and Phenolic Resin in Ethyl Acetate, Cured on Semi-Cured Phenolic Sheet

Podolsky (Wirt Company, US 2,060,114, 1936) bonded the carbon film into its base: the phenolic sheet is only half cured, the coating carries the same kind of resin, and its solvent (ethyl acetate) softens the sheet's surface. Heated calender rolls then finish the cure of sheet and coating together, so the track is hard, does not rub off and lasts. Cut across, the sheet gives resistance strips for a variable resistor. The picture: our diagram.
Menengah
1 day

Instruksi

1

Mix 21 carbon, 26 resin, 53 solvent

Make a solution of 21 % carbon, 26 % phenol-formaldehyde resin and 53 % ethyl acetate. The patent says the exact proportions are not essential; this is its example.

Material untuk langkah ini:

KarbonKarbon21 parts
Bakelit Cair (Produk Kondensasi Fenol-Formaldehida)Bakelit Cair (Produk Kondensasi Fenol-Formaldehida)26 parts

Alat yang dibutuhkan:

Etil AsetatEtil Asetat
Neraca lenganNeraca lengan
Gelas Beker KacaGelas Beker Kaca
PengadukPengaduk
Respirator wajah penuhRespirator wajah penuh
Sarung tangan karetSarung tangan karet
2

Coat the semi-cured sheet

Use a phenolic sheet whose cure was stopped before it fully hardened. A roller turning in a pan of the solution coats its underside.

Material untuk langkah ini:

Lembaran Fenolik Setengah MatangLembaran Fenolik Setengah Matang1 buah

Alat yang dibutuhkan:

Sepasang Rol Pelapis CelupSepasang Rol Pelapis Celup
Respirator wajah penuhRespirator wajah penuh
Sarung tangan karetSarung tangan karet
3

Cure between calender rolls at 350 °F

Pass the coated sheet between calender rolls heated to about 350 °F (177 °C). This finishes the cure and bonds the coating to the sheet. The patent sometimes calenders it again to burnish the surface.

Alat yang dibutuhkan:

Rol Kalender BerpemanasRol Kalender Berpemanas
Sarung Tangan Tahan PanasSarung Tangan Tahan Panas
4

Cut into strips

Cut the sheet across into strips of the width wanted. Ours: tin snips.

Alat yang dibutuhkan:

Gunting sengGunting seng
Sarung tangan karetSarung tangan karet

Bahan

3

Alat yang Diperlukan

10

Cetak biru ini membuat

Thumbnail
Placeholder

Elemen Resistansi Karbon

Free

10
0
1

Blueprint terkait

Blueprint ini berbagi pengetahuan — teknik, bahan, atau prinsip

Liquid Bakelite: Phenol and Formalin Heated Together, the Oily Layer Kept (Baekeland 1909)
Berbahaya

Liquid Bakelite: Phenol and Formalin Heated Together, the Oily Layer Kept (Baekeland 1909)

oleh CharlieDE

Industri

7
0
0
0
0
0
Carbon Resistance Element: Lampblack in Alkyd and Chinese Wood Oil on Laminated Phenolic

Carbon Resistance Element: Lampblack in Alkyd and Chinese Wood Oil on Laminated Phenolic

oleh EdFI

Elektronik

11
0
0
0
0
0

CC0 Domain Publik

Cetak biru ini dirilis di bawah CC0. Anda bebas untuk menyalin, memodifikasi, mendistribusikan, dan menggunakan karya ini untuk tujuan apa pun, termasuk komersial, tanpa meminta izin.

Dukung Maker dengan membeli produk melalui Cetak Biru mereka di mana mereka mendapatkan Komisi Pembuat yang ditetapkan oleh Penjual, atau buat iterasi baru dari Cetak Biru ini dan masukkan sebagai koneksi di milik Anda sendiri.

Diskusi

(0)

Masuk untuk bergabung dengan diskusi

Memuat komentar...