Ferrite Toroid Core: Copper-Zinc Ferrite Fired at 1050 °C, Held at 600 °C in Oxygen (Snoek)
Charlie

Dibuat oleh

Charlie

21. Oktober 2026DE
12
0
0
0
0

Ferrite Toroid Core: Copper-Zinc Ferrite Fired at 1050 °C, Held at 600 °C in Oxygen (Snoek)

Ferrite is a ceramic magnet: iron oxide combined with other metal oxides, carrying magnetic flux while hardly conducting electricity. Snoek at Philips (US 2,452,531, 1948) made this copper-zinc ferrite ring at a lower heat: technical copper oxide, zinc oxide and iron oxide with 1 % brownstone, fired at 1050 °C, then held 14 hours at 600 °C, all in oxygen. His ring had an initial permeability of 385. The picture: our diagram.
Lanjutan
2 days

Instruksi

1

Mix 20.7 : 31.6 : 47.7 mol + 1 % brownstone

Mix technical copper oxide, zinc oxide and iron oxide in the molecular ratio 20.7 : 31.6 : 47.7 (on the pure oxides) and add 1 % by weight of brownstone (manganese dioxide). Ours, by weight: 13.91 g copper oxide, 21.73 g zinc oxide and 64.36 g ferric oxide per 100 g, plus 1 g brownstone.

Material untuk langkah ini:

Tembaga OksidaTembaga Oksida13.91 g
Serbuk Seng OksidaSerbuk Seng Oksida21.73 g
Besi(III) OksidaBesi(III) Oksida64.36 g
Mangan dioksida (pirolusit)Mangan dioksida (pirolusit)1 g

Alat yang dibutuhkan:

Neraca lenganNeraca lengan
Masker DebuMasker Debu
2

Grind for 3 hours in an iron ball mill

Grind the mixture for 3 hours in a mill with iron balls.

Alat yang dibutuhkan:

Ball Mill BesiBall Mill Besi
Masker DebuMasker Debu
3

Mould a ring at 4 tons per cm²

Mould a ring 3 cm across and 4 × 4 mm in section at 4 tons per square centimetre, with water as the plastifying and binding agent.

Alat yang dibutuhkan:

Mesin pres hidrolikMesin pres hidrolik
Cetakan Penekan CincinCetakan Penekan Cincin
Air SulingAir Suling
4

Fire 1 hour at 1050 °C, hold 14 hours at 600 °C

Sinter the ring in oxygen at 1050 °C for 1 hour, cool it slowly to 600 °C and hold it there for 14 hours, all in oxygen, then let it cool further. Snoek's core had an initial permeability of 385.

Alat yang dibutuhkan:

Tungku TabungTungku Tabung
OksigenOksigen
Tabung gas bertekananTabung gas bertekanan
PirometerPirometer
Penjepit KowiPenjepit Kowi
Sarung Tangan Tahan PanasSarung Tangan Tahan Panas

Bahan

4

Alat yang Diperlukan

12

Cetak biru ini membuat

Thumbnail
Placeholder

Inti Toroid Ferit

Free

251
0
1

Blueprint terkait

Blueprint ini berbagi pengetahuan — teknik, bahan, atau prinsip

Ferrite Toroid Core: Nickel-Zinc Ferrite Sintered at 1300 °C in Oxygen (Snoek)
Berbahaya

Ferrite Toroid Core: Nickel-Zinc Ferrite Sintered at 1300 °C in Oxygen (Snoek)

oleh CharlieDE

Industri

12
0
0
0
0
0
Ferric Oxide: Hydroxide Precipitated from Ferric Chloride with Ammonia, Then Heated

Ferric Oxide: Hydroxide Precipitated from Ferric Chloride with Ammonia, Then Heated

oleh CharlieDE

Anorganik

5
0
0
0
0
0
Copper(II) Oxide by Heating Copper in Air

Copper(II) Oxide by Heating Copper in Air

oleh CharlieDE

Kimia

23
0
0
0
0
0

CC0 Domain Publik

Cetak biru ini dirilis di bawah CC0. Anda bebas untuk menyalin, memodifikasi, mendistribusikan, dan menggunakan karya ini untuk tujuan apa pun, termasuk komersial, tanpa meminta izin.

Dukung Maker dengan membeli produk melalui Cetak Biru mereka di mana mereka mendapatkan Komisi Pembuat yang ditetapkan oleh Penjual, atau buat iterasi baru dari Cetak Biru ini dan masukkan sebagai koneksi di milik Anda sendiri.

Diskusi

(0)

Masuk untuk bergabung dengan diskusi

Memuat komentar...