Ferrite Toroid Core: Copper-Zinc Ferrite Sintered at 1200 °C (Snoek 1948, Ex. I)
Charlie

Dibuat oleh

Charlie

28. Oktober 2026DE
1
0
0
0
0

Ferrite Toroid Core: Copper-Zinc Ferrite Sintered at 1200 °C (Snoek 1948, Ex. I)

A soft ferrite ring core for coils and transformers: copper, zinc and iron oxides with a little brownstone, pressed into a ring and sintered at 1200 °C in oxygen. Snoek's ring had an initial permeability of 285. Source: J. L. Snoek, US 2,452,530 (Philips, 1948), Example I and its table. Unknown: the 'violet' iron oxide, linked to an unknown head. Picture: the patent's Fig. 4, the ring core.
Lanjutan
2 days

Instruksi

1

Weigh 20 : 30 : 50 mol % and 1 % brownstone

Mix 20 mol % pure copper oxide, 30 mol % pure zinc oxide and 50 mol % pure violet iron oxide, and add 1 % by weight of brownstone (manganese dioxide). Ours, by weight: 13.24 g copper oxide, 20.32 g zinc oxide and 66.44 g iron oxide per 100 g, plus 1 g brownstone. Unknown: what makes the iron oxide 'violet'; Snoek does not say.

Material untuk langkah ini:

Tembaga OksidaTembaga Oksida13.24 g
Serbuk Seng OksidaSerbuk Seng Oksida20.32 g
Oksida besi unguOksida besi ungu66.44 g
Mangan dioksida (pirolusit)Mangan dioksida (pirolusit)1 g

Alat yang dibutuhkan:

Neraca lenganNeraca lengan
Masker DebuMasker Debu
2

Grind half an hour in an iron ball mill

Grind the mixture for half an hour in a mill with iron balls.

Alat yang dibutuhkan:

Ball Mill BesiBall Mill Besi
Masker DebuMasker Debu
3

Press a ring at 4 tons per cm²

Press the powder at 4 tons per square centimetre into a ring 3 cm across with a 4 × 4 mm cross-section.

Alat yang dibutuhkan:

Mesin pres hidrolikMesin pres hidrolik
Cetakan Penekan CincinCetakan Penekan Cincin
Masker DebuMasker Debu
4

Sinter at 1200 °C in oxygen, cool 5–10 °C a minute

Sinter the ring at 1200 °C in a current of oxygen. Example I heats for 1 hour and cools in the oxygen at 5 to 10 °C per minute. Snoek's ring had an initial permeability of 285, measured at room temperature at 2 kHz.

Alat yang dibutuhkan:

Tungku TabungTungku Tabung
OksigenOksigen
Tabung gas bertekananTabung gas bertekanan
PirometerPirometer
Penjepit KowiPenjepit Kowi
Sarung Tangan Tahan PanasSarung Tangan Tahan Panas

Bahan

4

Alat yang Diperlukan

11

Cetak biru ini membuat

Thumbnail
Placeholder

Inti Toroid Ferit

Free

252
0
1

Blueprint terkait

Blueprint ini berbagi pengetahuan — teknik, bahan, atau prinsip

Ferrite Toroid Core: Nickel-Zinc Ferrite Sintered at 1300 °C in Oxygen (Snoek)
Berbahaya

Ferrite Toroid Core: Nickel-Zinc Ferrite Sintered at 1300 °C in Oxygen (Snoek)

oleh CharlieDE

Industri

13
0
0
0
0
0
Copper(II) Oxide by Heating Copper in Air

Copper(II) Oxide by Heating Copper in Air

oleh CharlieDE

Kimia

23
0
0
0
0
0

CC0 Domain Publik

Cetak biru ini dirilis di bawah CC0. Anda bebas untuk menyalin, memodifikasi, mendistribusikan, dan menggunakan karya ini untuk tujuan apa pun, termasuk komersial, tanpa meminta izin.

Dukung Maker dengan membeli produk melalui Cetak Biru mereka di mana mereka mendapatkan Komisi Pembuat yang ditetapkan oleh Penjual, atau buat iterasi baru dari Cetak Biru ini dan masukkan sebagai koneksi di milik Anda sendiri.

Diskusi

(0)

Masuk untuk bergabung dengan diskusi

Memuat komentar...