Ferrite Toroid Core: Copper-Zinc Ferrite by the Wet Process, Precipitated with Caustic Soda (Snoek 1948)
Charlie

Dibuat oleh

Charlie

28. Oktober 2026DE
3
0
0
0
0

Ferrite Toroid Core: Copper-Zinc Ferrite by the Wet Process, Precipitated with Caustic Soda (Snoek 1948)

Snoek's copper-zinc ferrite made the wet way: copper, zinc and iron salts thrown down together with hot caustic soda, so the particles are very fine and pure. The washed deposit is pre-heated, pressed into a ring and fired in oxygen, with a 30-hour hold at 600 °C. His core reached an initial permeability of 500. Source: J. L. Snoek, US 2,452,529 (Philips, 1948), Example II, wet process. Picture: our diagram.
Lanjutan
3 days

Instruksi

1

Dissolve the copper, zinc and iron salts

Make 1 litre of a purified solution of 0.2 mol copper sulphate, 0.3 mol zinc sulphate and 1 mol iron nitrate. Ours: 49.94 g copper sulphate pentahydrate; weigh the zinc sulphate and ferric nitrate for the hydrate you have.

Material untuk langkah ini:

Tembaga sulfat pentahidrat (CuSO4·5H2O)Tembaga sulfat pentahidrat (CuSO4·5H2O)49.94 g
Seng sulfatSeng sulfat0.3 mol
Feri NitratFeri Nitrat1 mol
Air SulingAir Suling1 l

Alat yang dibutuhkan:

Neraca lenganNeraca lengan
Gelas Piala BorosilikatGelas Piala Borosilikat
Sarung tangan karetSarung tangan karet
2

Precipitate hot with 9 M caustic soda

Heat the solution and precipitate it with 0.5 litre of 9 molar caustic soda. Ours: 180 g sodium hydroxide in water to 0.5 litre. Strong alkali: goggles and gloves.

Material untuk langkah ini:

Natrium Hidroksida — Mutu LaboratoriumNatrium Hidroksida — Mutu Laboratorium180 g

Alat yang dibutuhkan:

Gelas Piala BorosilikatGelas Piala Borosilikat
Pelat PemanasPelat Pemanas
Kacamata Pelindung Cipratan KimiaKacamata Pelindung Cipratan Kimia
Sarung tangan karetSarung tangan karet
3

Wash, dry and pre-heat at 700 °C

Wash out the deposit, dry it, and pre-heat it at 700 °C so it moulds better.

Alat yang dibutuhkan:

Kertas SaringKertas Saring
Air SulingAir Suling
Oven pengeringanOven pengeringan
Tungku TabungTungku Tabung
Krus dengan tutup (porselen)Krus dengan tutup (porselen)
Sarung Tangan Tahan PanasSarung Tangan Tahan Panas
4

Mould a ring at 4 tons per cm²

Mould the powder at 4 tons per square centimetre into a ring 3 cm across with a 4 × 4 mm section.

Alat yang dibutuhkan:

Mesin pres hidrolikMesin pres hidrolik
Cetakan Penekan CincinCetakan Penekan Cincin
Masker DebuMasker Debu
5

Heat 3 hours at 900 °C, cool to 600 °C, hold 30 hours

Heat the ring for about 3 hours at 900 °C, cool it to 600 °C at 5 °C per minute, hold it there for 30 hours and let it cool to room temperature, all in a current of oxygen. Snoek's core: initial permeability 500.

Alat yang dibutuhkan:

Tungku TabungTungku Tabung
OksigenOksigen
Tabung gas bertekananTabung gas bertekanan
PirometerPirometer
Penjepit KowiPenjepit Kowi
Sarung Tangan Tahan PanasSarung Tangan Tahan Panas

Bahan

5

Alat yang Diperlukan

18

Cetak biru ini membuat

Thumbnail
Placeholder

Inti Toroid Ferit

Free

251
0
1

Blueprint terkait

Blueprint ini berbagi pengetahuan — teknik, bahan, atau prinsip

Ferrite Toroid Core: Copper-Zinc Ferrite Milled 200 Hours, Fired at 1050 °C (Snoek)

Ferrite Toroid Core: Copper-Zinc Ferrite Milled 200 Hours, Fired at 1050 °C (Snoek)

oleh CharlieDE

Industri

10
0
0
0
0
0
Ferric Nitrate: Scrap Iron Dissolved in Concentrated Nitric Acid (Thorpe 1912)
Berbahaya

Ferric Nitrate: Scrap Iron Dissolved in Concentrated Nitric Acid (Thorpe 1912)

oleh CharlieDE

Industri

2
0
0
0
0
0

CC0 Domain Publik

Cetak biru ini dirilis di bawah CC0. Anda bebas untuk menyalin, memodifikasi, mendistribusikan, dan menggunakan karya ini untuk tujuan apa pun, termasuk komersial, tanpa meminta izin.

Dukung Maker dengan membeli produk melalui Cetak Biru mereka di mana mereka mendapatkan Komisi Pembuat yang ditetapkan oleh Penjual, atau buat iterasi baru dari Cetak Biru ini dan masukkan sebagai koneksi di milik Anda sendiri.

Diskusi

(0)

Masuk untuk bergabung dengan diskusi

Memuat komentar...