Ferrite Toroid Core: Magnesium-Zinc Ferrite Fired at 1400 °C in Oxygen (Snoek)
Charlie

Dibuat oleh

Charlie

21. Oktober 2026DE
7
0
0
0
0

Ferrite Toroid Core: Magnesium-Zinc Ferrite Fired at 1400 °C in Oxygen (Snoek)

Ferrite is a ceramic magnet: iron oxide combined with other metal oxides, carrying magnetic flux while hardly conducting electricity. Snoek at Philips (US 2,452,531, 1948) made this magnesium-zinc ferrite ring: magnesia, zinc oxide and iron oxide ground together, moulded with water into a ring and fired in oxygen at 1400 °C for 1 hour, then cooled slowly. His ring had an initial permeability of 525. The picture: our diagram.
Lanjutan
2 days

Instruksi

1

Mix 26.5 : 26.5 : 47 mol

Mix pure magnesium oxide, zinc oxide and iron oxide in the molecular ratio 26.5 : 26.5 : 47. Ours, by weight: 9.95 g magnesium oxide, 20.10 g zinc oxide and 69.95 g ferric oxide per 100 g.

Material untuk langkah ini:

Magnesium oksidaMagnesium oksida9.95 g
Serbuk Seng OksidaSerbuk Seng Oksida20.1 g
Besi(III) OksidaBesi(III) Oksida69.95 g

Alat yang dibutuhkan:

Neraca lenganNeraca lengan
Masker DebuMasker Debu
2

Grind for 3 hours in an iron ball mill

Grind the mixture for 3 hours in a mill with iron balls.

Alat yang dibutuhkan:

Ball Mill BesiBall Mill Besi
Masker DebuMasker Debu
3

Mould a ring at 4 tons per cm²

Mould a ring 3 cm across and 4 × 4 mm in section at 4 tons per square centimetre, with water as the plastifying and binding agent.

Alat yang dibutuhkan:

Mesin pres hidrolikMesin pres hidrolik
Cetakan Penekan CincinCetakan Penekan Cincin
Air SulingAir Suling
4

Fire 1 hour at 1400 °C, cool at 3 °C a minute

Heat the ring in oxygen to 1400 °C for 1 hour (instead of 1300 °C), then cool it in oxygen at about 3 °C per minute. Snoek's ring had an initial permeability of 525.

Alat yang dibutuhkan:

Tungku TabungTungku Tabung
OksigenOksigen
Tabung gas bertekananTabung gas bertekanan
PirometerPirometer
Penjepit KowiPenjepit Kowi
Sarung Tangan Tahan PanasSarung Tangan Tahan Panas

Bahan

3

Alat yang Diperlukan

12

Cetak biru ini membuat

Thumbnail
Placeholder

Inti Toroid Ferit

Free

251
0
1

Blueprint terkait

Blueprint ini berbagi pengetahuan — teknik, bahan, atau prinsip

Ferrite Toroid Core: Nickel-Zinc Ferrite Sintered at 1300 °C in Oxygen (Snoek)
Berbahaya

Ferrite Toroid Core: Nickel-Zinc Ferrite Sintered at 1300 °C in Oxygen (Snoek)

oleh CharlieDE

Industri

12
0
0
0
0
0
Ferric Oxide: Hydroxide Precipitated from Ferric Chloride with Ammonia, Then Heated

Ferric Oxide: Hydroxide Precipitated from Ferric Chloride with Ammonia, Then Heated

oleh CharlieDE

Anorganik

5
0
0
0
0
0

CC0 Domain Publik

Cetak biru ini dirilis di bawah CC0. Anda bebas untuk menyalin, memodifikasi, mendistribusikan, dan menggunakan karya ini untuk tujuan apa pun, termasuk komersial, tanpa meminta izin.

Dukung Maker dengan membeli produk melalui Cetak Biru mereka di mana mereka mendapatkan Komisi Pembuat yang ditetapkan oleh Penjual, atau buat iterasi baru dari Cetak Biru ini dan masukkan sebagai koneksi di milik Anda sendiri.

Diskusi

(0)

Masuk untuk bergabung dengan diskusi

Memuat komentar...