Ferrite Toroid Core: Magnesium-Zinc Ferrite (28 : 18 : 54) Fired at 1400 °C (Snoek)
Charlie

Dibuat oleh

Charlie

21. Oktober 2026DE
8
0
0
0
0

Ferrite Toroid Core: Magnesium-Zinc Ferrite (28 : 18 : 54) Fired at 1400 °C (Snoek)

Ferrite is a ceramic magnet: iron oxide combined with other metal oxides, carrying magnetic flux while hardly conducting electricity. In his first ferrite patent (US 2,452,529, 1948) Snoek at Philips ground the oxides very fine and fired rings in oxygen. This magnesium-zinc ferrite (28 : 18 : 54 mol %) is milled 30 hours and fired 2 hours at 1400 °C; his core had an initial permeability of 150. The picture: our diagram.
Lanjutan
3 days

Instruksi

1

Mix 28 : 18 : 54 mol

Mix pure magnesium oxide, zinc oxide and ferric oxide, 28 : 18 : 54 mol %. Ours, by weight: 10.06 g magnesium oxide, 13.06 g zinc oxide and 76.88 g ferric oxide per 100 g.

Material untuk langkah ini:

Magnesium oksidaMagnesium oksida10.06 g
Serbuk Seng OksidaSerbuk Seng Oksida13.06 g
Besi(III) OksidaBesi(III) Oksida76.88 g

Alat yang dibutuhkan:

Neraca lenganNeraca lengan
Masker DebuMasker Debu
2

Grind 30 hours in an iron ball mill

Grind the mixture for 30 hours in an iron ball mill.

Alat yang dibutuhkan:

Ball Mill BesiBall Mill Besi
Masker DebuMasker Debu
3

Mould a ring at 4 tons per cm²

Press the powder at 4 tons per square centimetre into a ring 3 cm across with a 4 × 4 mm section.

Alat yang dibutuhkan:

Mesin pres hidrolikMesin pres hidrolik
Cetakan Penekan CincinCetakan Penekan Cincin
4

Fire 2 hours at 1400 °C, cool slowly

Heat the ring in oxygen for 2 hours at 1400 °C, then cool it slowly in oxygen at 5–10 °C a minute. Snoek's core: initial permeability 150.

Alat yang dibutuhkan:

Tungku TabungTungku Tabung
OksigenOksigen
Tabung gas bertekananTabung gas bertekanan
PirometerPirometer
Penjepit KowiPenjepit Kowi
Sarung Tangan Tahan PanasSarung Tangan Tahan Panas

Bahan

3

Alat yang Diperlukan

11

Cetak biru ini membuat

Thumbnail
Placeholder

Inti Toroid Ferit

Free

251
0
1

Blueprint terkait

Blueprint ini berbagi pengetahuan — teknik, bahan, atau prinsip

Ferrite Toroid Core: Nickel-Zinc Ferrite Sintered at 1300 °C in Oxygen (Snoek)
Berbahaya

Ferrite Toroid Core: Nickel-Zinc Ferrite Sintered at 1300 °C in Oxygen (Snoek)

oleh CharlieDE

Industri

10
0
0
0
0
0
Ferric Oxide: Hydroxide Precipitated from Ferric Chloride with Ammonia, Then Heated

Ferric Oxide: Hydroxide Precipitated from Ferric Chloride with Ammonia, Then Heated

oleh CharlieDE

Anorganik

5
0
0
0
0
0

CC0 Domain Publik

Cetak biru ini dirilis di bawah CC0. Anda bebas untuk menyalin, memodifikasi, mendistribusikan, dan menggunakan karya ini untuk tujuan apa pun, termasuk komersial, tanpa meminta izin.

Dukung Maker dengan membeli produk melalui Cetak Biru mereka di mana mereka mendapatkan Komisi Pembuat yang ditetapkan oleh Penjual, atau buat iterasi baru dari Cetak Biru ini dan masukkan sebagai koneksi di milik Anda sendiri.

Diskusi

(0)

Masuk untuk bergabung dengan diskusi

Memuat komentar...