Ferrite Toroid Core: Nickel-Zinc Ferrite Given a Further Oxygen Treatment (Snoek 1948, Ex. IV)
Berbahaya
Charlie

Dibuat oleh

Charlie

28. Oktober 2026DE
2
0
0
0
0

Ferrite Toroid Core: Nickel-Zinc Ferrite Given a Further Oxygen Treatment (Snoek 1948, Ex. IV)

Snoek's nickel-zinc ferrite ring (Example IV, initial permeability 560), given a further 12 hours at 1000 °C and 20 hours at 750 °C in oxygen. Unlike his magnesium-zinc core, its losses did not change. Nickel oxide dust is a cancer hazard: respirator when milling. Source: J. L. Snoek, US 2,452,529 (Philips, 1948), Example IV. Picture: our diagram.
Lanjutan
3 days

Konten berbahaya

Blueprint ini mengandung prosedur berbahaya. Masuk dan aktifkan konten berbahaya di pengaturan akun Anda untuk melihat petunjuk langkah demi langkah.

Masuk

Cetak biru ini membuat

Thumbnail
Placeholder

Inti Toroid Ferit

Free

251
0
1

Blueprint terkait

Blueprint ini berbagi pengetahuan — teknik, bahan, atau prinsip

Ferrite Toroid Core: Nickel-Zinc Ferrite Fired at 1400 °C, Held at 930 °C (Snoek)
Berbahaya

Ferrite Toroid Core: Nickel-Zinc Ferrite Fired at 1400 °C, Held at 930 °C (Snoek)

oleh CharlieDE

Industri

11
0
0
0
0
0

CC0 Domain Publik

Cetak biru ini dirilis di bawah CC0. Anda bebas untuk menyalin, memodifikasi, mendistribusikan, dan menggunakan karya ini untuk tujuan apa pun, termasuk komersial, tanpa meminta izin.

Dukung Maker dengan membeli produk melalui Cetak Biru mereka di mana mereka mendapatkan Komisi Pembuat yang ditetapkan oleh Penjual, atau buat iterasi baru dari Cetak Biru ini dan masukkan sebagai koneksi di milik Anda sendiri.

Diskusi

(0)

Masuk untuk bergabung dengan diskusi

Memuat komentar...