Neodymium Magnets: Melt-Spun Ribbon Milled, Pressed in a Field, Sintered and Magnetised at 30 kOe (Sato, Tokin, US 4,881,986)
Squirting the molten Nd-Fe-B alloy onto a spinning copper wheel freezes it into ribbon with crystals only a tenth of a micron across. Milled fine, lined up in a magnetic field, pressed and sintered, it makes a strong anisotropic magnet, which a 30 kOe pulse then magnetises.
Result: sintered neodymium magnets, above 16 MGOe when the powder is finer than 15 microns.
Source: Sato and Tachiya, US 4,881,986 (Tokin, 1989), Example 1. Not given: magnet shape and size. Picture drawn by Youblob.
Lanjutan
3 days
Instruksi
1
1
Melt the alloy in argon
Melt the alloy in argon
Weigh 35.0 % neodymium, 0.9 % boron (as ferroboron with 20 % B) and the rest electrolytic iron, by weight, and induction-melt them in argon into an ingot. Ours, worked out: 35 parts neodymium, 4.5 ferroboron, 60.5 iron. Sato's neodymium was 97 % (with Ce and Pr); ours is the 99 % metal.
Material untuk langkah ini:
Logam neodimium35 parts
Ferroboron4.5 parts
Besi elektrolitik60.5 partsAlat yang dibutuhkan:
Neraca lengan
Tanur induksi
Tabung gas bertekanan2
2
Melt-spin a ribbon
Melt-spin a ribbon
Remelt in argon and squirt the alloy through a small orifice onto a copper wheel whose rim moves at 15 m/s. It freezes into ribbon about 5 mm wide and 100 microns thick, with R2Fe14B grains about 0.1 micron.
Alat yang dibutuhkan:
Tanur induksi
Pemintal leburanTabung gas bertekanan3
3
Ball-mill to powder
Ball-mill to powder
Crush and ball-mill the ribbon. Particle size: Sato made 0.5 to 30 microns; below 15 microns the magnet tops 16 MGOe, better below 10, best at 5 microns or less.
Alat yang dibutuhkan:
Ball Mill Besi4
4
Press in a 20 kOe field and sinter
Press in a 20 kOe field and sinter
Press the powder at 1 ton/cm² in a 20 kOe field. Sinter at 1,050 °C for 1 hour in vacuum and 1 more hour in argon, then quench; age at 630 °C for 1 hour in argon.
Alat yang dibutuhkan:
Pres medan magnet
Tungku Tabung
Pompa vakumTabung gas bertekanan5
5
Magnetise at 30 kOe
Magnetise at 30 kOe
Magnetise the sintered body in a field of about 30 kOe.
Alat yang dibutuhkan:
PemagnetBahan
3- 35 partsPlaceholder
- 4.5 partsPlaceholder
- 60.5 partsPlaceholder
Alat yang Diperlukan
9- Placeholder
- Placeholder
- Placeholder
- Placeholder
- Placeholder
- Placeholder
- Placeholder
- 1 vendor sell this, none ship to you yetPlaceholder
- Placeholder
Cetak biru ini membuat
Blueprint terkait
Blueprint ini berbagi pengetahuan — teknik, bahan, atau prinsip
CC0 Domain Publik
Cetak biru ini dirilis di bawah CC0. Anda bebas untuk menyalin, memodifikasi, mendistribusikan, dan menggunakan karya ini untuk tujuan apa pun, termasuk komersial, tanpa meminta izin.
Dukung Maker dengan membeli produk melalui Cetak Biru mereka di mana mereka mendapatkan Komisi Pembuat yang ditetapkan oleh Penjual, atau buat iterasi baru dari Cetak Biru ini dan masukkan sebagai koneksi di milik Anda sendiri.