Metal Oxide Varistor: Zinc Oxide, 0.5 % Bismuth Oxide, 1 % Antimony Trioxide, 1350 °C (Masuyama 1972, Ex. 2)
Ed

Dibuat oleh

Ed

28. Oktober 2026FI
1
0
0
0
0

Metal Oxide Varistor: Zinc Oxide, 0.5 % Bismuth Oxide, 1 % Antimony Trioxide, 1350 °C (Masuyama 1972, Ex. 2)

Masuyama, Matsuoka and Nishi found that adding a second oxide to zinc oxide and bismuth oxide changes the varistor a great deal. This is their Example 2 with antimony trioxide: 98.5 % zinc oxide, 0.5 % bismuth oxide and 1.0 % antimony trioxide by moles, sintered at 1350 °C. The disc measured a C-value of 75 at 1 mA and a nonlinearity exponent n of 15.3. Source: T. Masuyama, M. Matsuoka and T. Nishi (Matsushita), US 3,663,458 (1972), Example 2. Unknown: how the aluminium is sprayed on and what the silver paint is. The 10 g batch is our arithmetic. Picture: the patent's drawing.
Lanjutan
1 day

Instruksi

1

Weigh 98.5 : 0.5 : 1 and wet-mill 5 hours

Mix zinc oxide, bismuth oxide and antimony trioxide 98.5 : 0.5 : 1 by moles. Ours, for 10 g: 9.386 g zinc oxide, 0.273 g bismuth oxide, 0.341 g antimony trioxide (our arithmetic). Mill wet for 5 hours, then dry. Unknown: the milling liquid.

Material untuk langkah ini:

Serbuk Seng OksidaSerbuk Seng Oksida9.386 g
Bismut oksidaBismut oksida0.273 g
Antimon trioksidaAntimon trioksida0.341 g

Alat yang dibutuhkan:

Neraca lenganNeraca lengan
Ball Mill BesiBall Mill Besi
Oven pengeringanOven pengeringan
2

Press discs 13 mm by 2.5 mm

Press the powder in a mould into discs 13 mm across and 2.5 mm thick at 340 kg/cm², as in Example 1.

Alat yang dibutuhkan:

Mesin pres hidrolikMesin pres hidrolik
Cetakan press cakramCetakan press cakram
Jangka Sorong VernierJangka Sorong Vernier
3

Sinter 1 hour at 1350 °C and furnace-cool

Sinter the discs in air for 1 hour at 1350 °C, then let them cool in the furnace to room temperature (about 15-30 °C).

Alat yang dibutuhkan:

Tungku MuffleTungku Muffle
4

Lap to 10 mm by 1.5 mm

Lap both faces with 600-mesh silicon carbide. The finished disc is 10 mm across and 1.5 mm thick.

Alat yang dibutuhkan:

Butiran silikon karbidaButiran silikon karbida
Jangka Sorong VernierJangka Sorong Vernier
5

Spray aluminium electrodes and attach leads

Spray a metallised film of aluminium on both faces. Attach a lead wire to each with conductive silver paint. Unknown: the spraying method and the paint.

Material untuk langkah ini:

Batangan aluminiumBatangan aluminium1 as required
Cat perak penghantar listrikCat perak penghantar listrik1 as required
Kawat TembagaKawat Tembaga2 buah

Alat yang dibutuhkan:

Metode semprot logam yang tidak diketahuiMetode semprot logam yang tidak diketahui
Jangka Sorong VernierJangka Sorong Vernier

Bahan

6

Alat yang Diperlukan

9

Cetak biru ini membuat

Thumbnail
Placeholder

Varistor oksida logam (penekan lonjakan)

Free

53
0
1

Blueprint terkait

Blueprint ini berbagi pengetahuan — teknik, bahan, atau prinsip

Metal Oxide Varistor: Zinc Oxide with 0.2 % Bismuth Oxide, Sintered Disc (Masuyama 1972)

Metal Oxide Varistor: Zinc Oxide with 0.2 % Bismuth Oxide, Sintered Disc (Masuyama 1972)

oleh EdFI

Industri

2
0
0
0
0
0

CC0 Domain Publik

Cetak biru ini dirilis di bawah CC0. Anda bebas untuk menyalin, memodifikasi, mendistribusikan, dan menggunakan karya ini untuk tujuan apa pun, termasuk komersial, tanpa meminta izin.

Dukung Maker dengan membeli produk melalui Cetak Biru mereka di mana mereka mendapatkan Komisi Pembuat yang ditetapkan oleh Penjual, atau buat iterasi baru dari Cetak Biru ini dan masukkan sebagai koneksi di milik Anda sendiri.

Diskusi

(0)

Masuk untuk bergabung dengan diskusi

Memuat komentar...