Zirconium: Oxide Reduced with Calcium and Calcium Chloride in a Sealed Bomb at 950 °C (Kiernan, US 1,760,413)

Pure zirconium nitrate is burnt to oxide, then sealed in a steel bomb with clean calcium chips and calcium chloride and held at 950 °C. Water washes out the calcium chloride and dilute nitric acid the lime, leaving zirconium powder. Result: dark grey zirconium metal powder, passing 150 mesh. Source: J. W. Kiernan (Westinghouse), US patent 1,760,413, pp. 2-3. Picture drawn by Youblob.

Lanjutan

3 days

Konten berbahaya

Blueprint ini mengandung prosedur berbahaya. Masuk dan aktifkan konten berbahaya di pengaturan akun Anda untuk melihat petunjuk langkah demi langkah.

Masuk

Cetak biru ini membuat

Placeholder

Zirkonium

Free

Blueprint terkait

Blueprint ini berbagi pengetahuan — teknik, bahan, atau prinsip

Berbahaya

Zirconium Nitrate: Zirconium Hydroxide Dissolved in Nitric Acid and Evaporated (Roscoe 1913)

oleh Charlie

Anorganik

Calcium: Anhydrous Calcium Iodide Reduced with Sodium in a Screwed Iron Crucible (Moissan, Thorpe 1912)

oleh Charlie

Anorganik

CC0 Domain Publik

Cetak biru ini dirilis di bawah CC0. Anda bebas untuk menyalin, memodifikasi, mendistribusikan, dan menggunakan karya ini untuk tujuan apa pun, termasuk komersial, tanpa meminta izin.

Dukung Maker dengan membeli produk melalui Cetak Biru mereka di mana mereka mendapatkan Komisi Pembuat yang ditetapkan oleh Penjual, atau buat iterasi baru dari Cetak Biru ini dan masukkan sebagai koneksi di milik Anda sendiri.

Diskusi

(0)

Masuk untuk bergabung dengan diskusi

Memuat komentar...