Oriented Barium Ferrite Disc Magnet: Water Instead of a Binder (Gorter, Philips 1956, Ex. 5)
A ceramic magnet from pre-fired barium ferrite powder stirred into water, oriented in a magnetic field in the die, moulded into blocks and fired as in Example 4. In the principal direction it held 2,870 gauss with a coercive force of 1,610 oersted and a (BH)max of 1.57 × 10⁶; at right angles 1,625 gauss.
Source: E. W. Gorter, G. W. Rathenau and A. L. Stuyts (Philips), US 2,762,778 (1956), Example 5. They made blocks; disc size is ours. Picture: ferrite magnets, Omegatron, Wikimedia Commons, CC BY-SA 3.0.
उन्नत
3 days
निर्देश
1
1
Weigh barium carbonate and iron oxide
Weigh barium carbonate and iron oxide
Weigh 450 g barium carbonate and 2000 g ferric oxide. Barium carbonate is poisonous if swallowed: gloves and a dust respirator.
इस चरण के लिए सामग्री:
बेरियम कार्बोनेट (विदराइट)450 ग्रा
फेरिक ऑक्साइड2000 ग्राआवश्यक उपकरण:
तराजू
रबर के दस्ताने
P100 श्वासयंत्र2
2
Mill 20 hours under alcohol, dry
Mill 20 hours under alcohol, dry
Grind the mixture in a ball mill under alcohol for 20 hours, then dry it.
आवश्यक उपकरण:
लोहे की बॉल मिल
एथेनॉल - प्रयोगशाला श्रेणी, 95 %
सुखाने की भट्ठी3
3
Pre-fire: through a 1100 °C zone in 10 minutes
Pre-fire: through a 1100 °C zone in 10 minutes
Pass the dry powder at 20 mm per minute through an electric furnace with a 20 cm hot zone at 1100 °C, in air: 10 minutes in the heat. Let it cool.
आवश्यक उपकरण:
ट्यूब फ़र्नेस
ढक्कन सहित मूषा (चीनी-मिट्टी)
ताप-रोधी दस्ताने4
4
Grind 12 hours with alcohol, dry
Grind 12 hours with alcohol, dry
Pulverise the pre-fired material in a ball mill with alcohol for 12 hours, then dry it. This is the pre-fired powder.
आवश्यक उपकरण:
लोहे की बॉल मिलएथेनॉल - प्रयोगशाला श्रेणी, 95 %सुखाने की भट्ठी5
5
Stir into water
Stir into water
Stir the pre-fired powder with water, 2 cc of water per gram of powder.
आवश्यक उपकरण:
आसुत जल6
6
Orient in a first field and mould
Orient in a first field and mould
Put the suspension in a moulding die, apply a first magnetic field and mould it into blocks. The patent does not give this field's strength.
आवश्यक उपकरण:
डिस्क दबाने की डाई
विद्युत-चुंबक
हाइड्रोलिक प्रेस7
7
Heat to 500 °C in a 2000 oersted field
Heat to 500 °C in a 2000 oersted field
Put the block in an electric furnace between the magnet's poles. With a second field of 2000 oersted along the first field's direction, heat to 500 °C, which burns off the rest of the binder. Then switch the field off.
आवश्यक उपकरण:
ट्यूब फ़र्नेसविद्युत-चुंबकताप-रोधी दस्ताने8
8
Sinter: through a 1280 °C zone in 5 minutes
Sinter: through a 1280 °C zone in 5 minutes
Pass the block at 20 mm per minute through an electric furnace in air at 1280 °C with a 10 cm hot zone: about 5 minutes in the heat.
आवश्यक उपकरण:
ट्यूब फ़र्नेसताप-रोधी दस्ताने9
9
Magnetise in the principal direction
Magnetise in the principal direction
Magnetise the block along the direction of the first field, the principal direction. The patent magnetises it in a field in that direction; ours: an electromagnet. Find the north face with a compass.
आवश्यक उपकरण:
विद्युत-चुंबक
दिक्सूचकसामग्री
2- 450 ग्राप्लेसहोल्डर
- 2000 ग्राप्लेसहोल्डर
आवश्यक उपकरण
14- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
यह ब्लूप्रिंट बनाता है
संबंधित ब्लूप्रिंट
ये ब्लूप्रिंट ज्ञान साझा करते हैं — तकनीक, सामग्री या सिद्धांत
CC0 पब्लिक डोमेन
यह ब्लूप्रिंट CC0 के तहत जारी किया गया है। आप बिना अनुमति माँगे इस कार्य को किसी भी उद्देश्य के लिए कॉपी, संशोधित, वितरित और उपयोग करने के लिए स्वतंत्र हैं।
उनके ब्लूप्रिंट के माध्यम से उत्पाद खरीदकर मेकर का समर्थन करें जहाँ वे मेकर कमीशन कमाते हैं जो विक्रेताओं द्वारा निर्धारित होता है, या इस ब्लूप्रिंट का नया संस्करण बनाएँ और राजस्व साझा करने के लिए इसे अपने ब्लूप्रिंट में कनेक्शन के रूप में शामिल करें।