Metal Oxide Varistor: Zinc Oxide, 0.5 % Bismuth Oxide, 0.5 % Boric Oxide, 1350 °C (Masuyama 1972, Ex. 2)
Masuyama, Matsuoka and Nishi found that adding a second oxide to zinc oxide and bismuth oxide changes the varistor a great deal. This is their Example 2 with boric oxide: 99 % zinc oxide, 0.5 % bismuth oxide and 0.5 % boric oxide by moles, sintered at 1350 °C. The disc measured a C-value of 6.5 at 1 mA and a nonlinearity exponent n of 5.7.
Source: T. Masuyama, M. Matsuoka and T. Nishi (Matsushita), US 3,663,458 (1972), Example 2. Unknown: what the silver paint is. The spraying is ours, after US Army Corps of Engineers EM 1110-2-3401 (1999). The 10 g batch is our arithmetic. Picture: the patent's drawing.
उन्नत
1 day
निर्देश
1
1
Weigh 99 : 0.5 : 0.5 and wet-mill 5 hours
Weigh 99 : 0.5 : 0.5 and wet-mill 5 hours
Mix zinc oxide, bismuth oxide and boric oxide 99 : 0.5 : 0.5 by moles. Ours, for 10 g: 9.678 g zinc oxide, 0.28 g bismuth oxide, 0.042 g boric oxide (our arithmetic). Mill wet for 5 hours, then dry. Unknown: the milling liquid.
इस चरण के लिए सामग्री:
ज़िंक ऑक्साइड चूर्ण9.678 ग्रा
बिस्मथ ऑक्साइड0.28 ग्रा
बोरिक ऑक्साइड0.042 ग्राआवश्यक उपकरण:
तराजू
लोहे की बॉल मिल
सुखाने की भट्ठी2
2
Press discs 13 mm by 2.5 mm
Press discs 13 mm by 2.5 mm
Press the powder in a mould into discs 13 mm across and 2.5 mm thick at 340 kg/cm², as in Example 1.
आवश्यक उपकरण:
हाइड्रोलिक प्रेस
डिस्क दबाने की डाई
वर्नियर कैलिपर3
3
Sinter 1 hour at 1350 °C and furnace-cool
Sinter 1 hour at 1350 °C and furnace-cool
Sinter the discs in air for 1 hour at 1350 °C, then let them cool in the furnace to room temperature (about 15-30 °C).
आवश्यक उपकरण:
मफल भट्ठी4
4
Lap to 10 mm by 1.5 mm
Lap to 10 mm by 1.5 mm
Lap both faces with 600-mesh silicon carbide. The finished disc is 10 mm across and 1.5 mm thick.
आवश्यक उपकरण:
सिलिकॉन कार्बाइड कणवर्नियर कैलिपर5
5
Spray aluminium electrodes and attach leads
Spray aluminium electrodes and attach leads
Spray a metallised film of aluminium on both faces. Attach a lead wire to each with conductive silver paint. Ours, after US Army Corps of Engineers EM 1110-2-3401 (1999): wire-arc spray the aluminium from two 3.2 mm wires melted by an 18-40 V DC arc and atomised by compressed air, 15-20 cm from the disc and never at less than 45°, in at least two coats at right angles of 50-75 µm each. Unknown: the paint.
इस चरण के लिए सामग्री:
ऐलुमिनियम की सिल्ली1 as 3.2 mm spray wire
चाँदी की चालक पेंट1 as required
ताँबे का तार2 टुकड़ेआवश्यक उपकरण:
वर्नियर कैलिपर
वायर-आर्क स्प्रे गन
औद्योगिक वायु संपीडकसामग्री
6- 9.678 ग्राप्लेसहोल्डर
- 0.28 ग्राप्लेसहोल्डर
- 0.042 ग्राप्लेसहोल्डर
- 1 as 3.2 mm spray wireप्लेसहोल्डर
- 1 as requiredप्लेसहोल्डर
- 2 टुकड़ेप्लेसहोल्डर
आवश्यक उपकरण
10- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
- प्लेसहोल्डर
यह ब्लूप्रिंट बनाता है
संबंधित ब्लूप्रिंट
ये ब्लूप्रिंट ज्ञान साझा करते हैं — तकनीक, सामग्री या सिद्धांत
CC0 पब्लिक डोमेन
यह ब्लूप्रिंट CC0 के तहत जारी किया गया है। आप बिना अनुमति माँगे इस कार्य को किसी भी उद्देश्य के लिए कॉपी, संशोधित, वितरित और उपयोग करने के लिए स्वतंत्र हैं।
उनके ब्लूप्रिंट के माध्यम से उत्पाद खरीदकर मेकर का समर्थन करें जहाँ वे मेकर कमीशन कमाते हैं जो विक्रेताओं द्वारा निर्धारित होता है, या इस ब्लूप्रिंट का नया संस्करण बनाएँ और राजस्व साझा करने के लिए इसे अपने ब्लूप्रिंट में कनेक्शन के रूप में शामिल करें।