Barium-Calcium Ferrite Disc Magnet: Equal Barium and Calcium, Sintered at 1280 °C (Went, Philips 1956, Ex. 22)
Omegatron (Wikimedia Commons) · CC BY-SA 3.0
Charlie

Búin til af

Charlie

28. október 2026DE
2
0
0
0
0

Barium-Calcium Ferrite Disc Magnet: Equal Barium and Calcium, Sintered at 1280 °C (Went, Philips 1956, Ex. 22)

A ceramic magnet with equal parts barium and calcium: 0.3 mol barium carbonate, 0.3 mol calcium carbonate and 3.1 mol iron oxide, milled 15 hours, pressed and passed through a 1280 °C furnace in 10 minutes, with no presintering. Went's rod held 1,595 gauss with a coercive force of 1,890 oersted. Source: J. J. Went, G. W. van Oosterhout and E. W. Gorter (Philips), US 2,762,777 (1956), Example 22. They sintered rods; discs and the magnetising are ours. Picture: ferrite magnets, Omegatron, Wikimedia Commons, CC BY-SA 3.0.
Lengra kominn
2 days

Leiðbeiningar

1

Weigh barium carbonate, chalk and iron oxide

Weigh 59.5 g barium carbonate (0.3 mol), 30.2 g calcium carbonate (0.3 mol) and 500.0 g ferric oxide (3.1 mol). Barium carbonate is poisonous if swallowed: gloves and a dust respirator.

Efni fyrir þetta skref:

Baríumkarbónat (witherít)Baríumkarbónat (witherít)59.5 g
Kalsíumkarbónat (kalkhvíta)Kalsíumkarbónat (kalkhvíta)30.2 g
Járn(III)oxíðJárn(III)oxíð500 g

Nauðsynleg verkfæri:

SkálavogSkálavog
GúmmíhanskarGúmmíhanskar
P100-öndunargrímaP100-öndunargríma
2

Mill with alcohol 15 hours, dry, press

Grind with alcohol in a ball mill for 15 hours, dry, and press at 1.5 tonnes per cm² (ours: discs instead of rods). No presintering.

Nauðsynleg verkfæri:

JárnkúlukvörnJárnkúlukvörn
Etanól - rannsóknargráða, 95 %Etanól - rannsóknargráða, 95 %
ÞurrkofnÞurrkofn
VökvapressaVökvapressa
Pressumót fyrir skífurPressumót fyrir skífur
3

Pass through a 1280 °C zone in 10 minutes

Sinter at 1280 °C by passing the pieces through a 10 cm hot zone at 10 mm per minute: 10 minutes in the heat.

Nauðsynleg verkfæri:

PípuofnPípuofn
Hitaþolnir hanskarHitaþolnir hanskar
4

Magnetise the discs

The patent gives no magnetising method. Ours: lay a disc with its faces against the poles of a strong electromagnet, switch the current on, then off. Find which face is north with a compass.

Nauðsynleg verkfæri:

RafmagnssegullRafmagnssegull
ÁttavitiÁttaviti

Efni

3

Nauðsynleg verkfæri

12

Þessi teikning býr til

Thumbnail
Tímabundinn texti

Skífusegull

Free

2
0
1

Tengd Blueprint

Þessi blueprint deila þekkingu — tækni, efni eða meginreglur

Barium Ferrite Disc Magnet: Barium Carbonate and Iron Oxide Sintered (Went, Philips 1956)

Barium Ferrite Disc Magnet: Barium Carbonate and Iron Oxide Sintered (Went, Philips 1956)

eftir CharlieDE

Iðnaður

2
0
0
0
0
0

CC0 opinbert ríki

Þessi teikning er gefin út undir CC0. Þér er frjálst að afrita, breyta, dreifa og nota þetta verk í hvaða tilgangi sem er, án þess að biðja um leyfi.

Studdu smiðinn með því að kaupa vörur í gegnum teikningu hans þar sem hann fær þóknun smiða sem seljendur ákvarða, eða búðu til nýja endurskoðun á þessari teikningu og tengdu hana sem tengingu í þinni eigin teikningu til að deila tekjum.

Umræða

(0)

Skrá inn til að taka þátt í umræðunni

Hleður athugasemdum...