Barium Ferrite Disc Magnet: Fired in Carbon Dioxide, Pressed at 12 t/cm² (Went, Philips 1956, Ex. 33)
A barium ferrite made with more iron oxide, 0.4 mol barium carbonate to 3.6 mol, fired an hour at 1300 °C in carbon dioxide. Little oxygen gives the hexagonal crystal BaFe18O27, with some iron in the lower state. It is milled again, bound with nitrocellulose or polyvinyl alcohol, and pressed hard at 12 tonnes per cm². Went's rod held 1,260 gauss with a coercive force of 700 oersted.
Source: J. J. Went, G. W. van Oosterhout and E. W. Gorter (Philips), US 2,762,777 (1956), Example 33. They sintered rods; discs and the magnetising are ours. Picture: ferrite magnets, Omegatron, Wikimedia Commons, CC BY-SA 3.0.
Lengra kominn
2 days
Leiðbeiningar
1
1
Weigh barium carbonate and iron oxide
Weigh barium carbonate and iron oxide
Weigh 79.4 g barium carbonate (0.4 mol) and 580.9 g ferric oxide (3.6 mol). Barium carbonate is poisonous if swallowed: gloves and a dust respirator.
Efni fyrir þetta skref:
Baríumkarbónat (witherít)79.4 g
Járn(III)oxíð580.9 gNauðsynleg verkfæri:
Skálavog
Gúmmíhanskar
P100-öndunargríma2
2
Mill 15.5 hours, press a pastille, fire in CO2
Mill 15.5 hours, press a pastille, fire in CO2
Grind with alcohol in a ball mill for 15.5 hours, dry, and press into a pastille. Heat it at 1300 °C in carbon dioxide for 1 hour (ours: a tube furnace fed from a CO2 cylinder).
Nauðsynleg verkfæri:
Járnkúlukvörn
Etanól - rannsóknargráða, 95 %
Þurrkofn
Vökvapressa
Pressumót fyrir skífur
Pípuofn
Koltvísýringsgas
Þrýstigaskútur
Hitaþolnir hanskar3
3
Pulverise, mill 14 hours, bind
Pulverise, mill 14 hours, bind
Crush the cooled pastille and grind it with alcohol for 14 hours. Press the powder into a pastille again with a ceramic binder (ours: polyvinyl alcohol, one of the two named), then crush it to grains.
Efni fyrir þetta skref:
Pólývínýlalkóhólduft1 as requiredNauðsynleg verkfæri:
JárnkúlukvörnEtanól - rannsóknargráða, 95 %VökvapressaPressumót fyrir skífur4
4
Press at 12 tonnes per cm²
Press at 12 tonnes per cm²
Press the grains at 12 tonnes per cm² (ours: discs instead of rods). The patent describes no further firing.
Nauðsynleg verkfæri:
VökvapressaPressumót fyrir skífur5
5
Magnetise the discs
Magnetise the discs
The patent gives no magnetising method. Ours: lay a disc with its faces against the poles of a strong electromagnet, switch the current on, then off. Find which face is north with a compass.
Nauðsynleg verkfæri:
Rafmagnssegull
ÁttavitiEfni
3- Staðgengill
- 580.9 gStaðgengill
- 1 as requiredStaðgengill
Nauðsynleg verkfæri
14- Staðgengill
- Staðgengill
- Staðgengill
- Staðgengill
- Staðgengill
- Staðgengill
- Staðgengill
- Staðgengill
- Staðgengill
- Staðgengill
- Staðgengill
- Staðgengill
- Staðgengill
- Staðgengill
Þessi teikning býr til
Tengd Blueprint
Þessi blueprint deila þekkingu — tækni, efni eða meginreglur
CC0 opinbert ríki
Þessi teikning er gefin út undir CC0. Þér er frjálst að afrita, breyta, dreifa og nota þetta verk í hvaða tilgangi sem er, án þess að biðja um leyfi.
Studdu smiðinn með því að kaupa vörur í gegnum teikningu hans þar sem hann fær þóknun smiða sem seljendur ákvarða, eða búðu til nýja endurskoðun á þessari teikningu og tengdu hana sem tengingu í þinni eigin teikningu til að deila tekjum.