Barium-Lead Ferrite Disc Magnet: 0.35 mol BaCO3 and 0.3 mol PbO2, 1145 °C (Went, Philips 1956, Ex. 32)
A ceramic magnet with both barium and lead: 0.35 mol barium carbonate and 0.3 mol lead dioxide to 3.4 mol iron oxide, milled 15.5 hours, presintered by heating slowly to 900 °C, pressed and passed through a 1145 °C furnace in 4 minutes. Went's rod held 1,785 gauss with a coercive force of 2,840 oersted. Barium and lead compounds are poisonous.
Source: J. J. Went, G. W. van Oosterhout and E. W. Gorter (Philips), US 2,762,777 (1956), Example 32. They sintered rods; discs and the magnetising are ours. Picture: ferrite magnets, Omegatron, Wikimedia Commons, CC BY-SA 3.0.
Lengra kominn
2 days
Hættulegt efni
Þessi teikning inniheldur hættulegar aðferðir. Skráðu þig inn og virkjaðu hættulegt efni í stillingum reikningsins til að sjá skref-fyrir-skref leiðbeiningar.
Skrá innÞessi teikning býr til
Tengd Blueprint
Þessi blueprint deila þekkingu — tækni, efni eða meginreglur
CC0 opinbert ríki
Þessi teikning er gefin út undir CC0. Þér er frjálst að afrita, breyta, dreifa og nota þetta verk í hvaða tilgangi sem er, án þess að biðja um leyfi.
Studdu smiðinn með því að kaupa vörur í gegnum teikningu hans þar sem hann fær þóknun smiða sem seljendur ákvarða, eða búðu til nýja endurskoðun á þessari teikningu og tengdu hana sem tengingu í þinni eigin teikningu til að deila tekjum.