Barium-Strontium Ferrite Disc Magnet: 0.21 mol BaCO3, 0.09 mol SrCO3, 1300 °C (Went, Philips 1956, Ex. 30)
Omegatron (Wikimedia Commons) · CC BY-SA 3.0
Charlie

Búin til af

Charlie

28. október 2026DE
2
0
0
0
0

Barium-Strontium Ferrite Disc Magnet: 0.21 mol BaCO3, 0.09 mol SrCO3, 1300 °C (Went, Philips 1956, Ex. 30)

A ceramic magnet with both barium and strontium: 0.21 mol barium carbonate and 0.09 mol strontium carbonate to 2.7 mol iron oxide, milled as in Example 28, pressed and passed through a 1300 °C furnace in 10 minutes. Went's rod held 1,245 gauss with a coercive force of 2,370 oersted. Source: J. J. Went, G. W. van Oosterhout and E. W. Gorter (Philips), US 2,762,777 (1956), Example 30. They sintered rods; discs and the magnetising are ours. Picture: ferrite magnets, Omegatron, Wikimedia Commons, CC BY-SA 3.0.
Lengra kominn
2 days

Leiðbeiningar

1

Weigh the carbonates and iron oxide

Weigh 41.7 g barium carbonate (0.21 mol), 13.3 g strontium carbonate (0.09 mol), 435.5 g ferric oxide (2.7 mol). Barium carbonate is poisonous if swallowed: gloves and a dust respirator.

Efni fyrir þetta skref:

Baríumkarbónat (witherít)Baríumkarbónat (witherít)41.7 g
StrontíumkarbónatStrontíumkarbónat13.3 g
Járn(III)oxíðJárn(III)oxíð435.5 g

Nauðsynleg verkfæri:

SkálavogSkálavog
GúmmíhanskarGúmmíhanskar
P100-öndunargrímaP100-öndunargríma
2

Mill with alcohol 15 hours, dry

As in Example 28: grind the mixture with alcohol in a ball mill for 15 hours, then dry it.

Nauðsynleg verkfæri:

JárnkúlukvörnJárnkúlukvörn
Etanól - rannsóknargráða, 95 %Etanól - rannsóknargráða, 95 %
ÞurrkofnÞurrkofn
3

Press the powder

Example 28 moulds a rod without giving the pressure. Ours: press discs at 1.5 tonnes per cm², the pressure of the patent's other examples.

Nauðsynleg verkfæri:

VökvapressaVökvapressa
Pressumót fyrir skífurPressumót fyrir skífur
4

Pass through a 1300 °C zone in 10 minutes

Sinter in air at 1300 °C by passing the pieces through a 10 cm hot zone at 10 mm per minute: 10 minutes in the heat.

Nauðsynleg verkfæri:

PípuofnPípuofn
Hitaþolnir hanskarHitaþolnir hanskar
5

Magnetise the discs

The patent gives no magnetising method. Ours: lay a disc with its faces against the poles of a strong electromagnet, switch the current on, then off. Find which face is north with a compass.

Nauðsynleg verkfæri:

RafmagnssegullRafmagnssegull
ÁttavitiÁttaviti

Efni

3

Nauðsynleg verkfæri

12

Þessi teikning býr til

Thumbnail
Tímabundinn texti

Skífusegull

Free

2
0
1

Tengd Blueprint

Þessi blueprint deila þekkingu — tækni, efni eða meginreglur

Barium Ferrite Disc Magnet: Barium Carbonate and Iron Oxide Sintered (Went, Philips 1956)

Barium Ferrite Disc Magnet: Barium Carbonate and Iron Oxide Sintered (Went, Philips 1956)

eftir CharlieDE

Iðnaður

2
0
0
0
0
0
Strontium Carbonate: Powdered Celestine Boiled with Soda Solution (Thorpe 1912)

Strontium Carbonate: Powdered Celestine Boiled with Soda Solution (Thorpe 1912)

eftir CharlieDE

Iðnaður

6
0
0
0
0
0

CC0 opinbert ríki

Þessi teikning er gefin út undir CC0. Þér er frjálst að afrita, breyta, dreifa og nota þetta verk í hvaða tilgangi sem er, án þess að biðja um leyfi.

Studdu smiðinn með því að kaupa vörur í gegnum teikningu hans þar sem hann fær þóknun smiða sem seljendur ákvarða, eða búðu til nýja endurskoðun á þessari teikningu og tengdu hana sem tengingu í þinni eigin teikningu til að deila tekjum.

Umræða

(0)

Skrá inn til að taka þátt í umræðunni

Hleður athugasemdum...