Ferrite Toroid Core: Copper-Zinc Ferrite by the Wet Process, Precipitated with Caustic Soda (Snoek 1948)
Charlie

Búin til af

Charlie

28. október 2026DE
8
0
0
0
0

Ferrite Toroid Core: Copper-Zinc Ferrite by the Wet Process, Precipitated with Caustic Soda (Snoek 1948)

Snoek's copper-zinc ferrite made the wet way: copper, zinc and iron salts thrown down together with hot caustic soda, so the particles are very fine and pure. The washed deposit is pre-heated, pressed into a ring and fired in oxygen, with a 30-hour hold at 600 °C. His core reached an initial permeability of 500. Source: J. L. Snoek, US 2,452,529 (Philips, 1948), Example II, wet process. Picture: our diagram.
Lengra kominn
3 days

Leiðbeiningar

1

Dissolve the copper, zinc and iron salts

Make 1 litre of a purified solution of 0.2 mol copper sulphate, 0.3 mol zinc sulphate and 1 mol iron nitrate. Ours: 49.94 g copper sulphate pentahydrate; weigh the zinc sulphate and ferric nitrate for the hydrate you have.

Efni fyrir þetta skref:

Koparsúlfat pentahýdrat (CuSO4·5H2O)Koparsúlfat pentahýdrat (CuSO4·5H2O)49.94 g
SinksúlfatSinksúlfat0.3 mol
Járn(III)nítratJárn(III)nítrat1 mol
Eimað vatnEimað vatn1 l

Nauðsynleg verkfæri:

SkálavogSkálavog
Bikarglas úr bórsílíkatiBikarglas úr bórsílíkati
GúmmíhanskarGúmmíhanskar
2

Precipitate hot with 9 M caustic soda

Heat the solution and precipitate it with 0.5 litre of 9 molar caustic soda. Ours: 180 g sodium hydroxide in water to 0.5 litre. Strong alkali: goggles and gloves.

Efni fyrir þetta skref:

Natríumhýdroxíð — rannsóknarstofugæðiNatríumhýdroxíð — rannsóknarstofugæði180 g

Nauðsynleg verkfæri:

Bikarglas úr bórsílíkatiBikarglas úr bórsílíkati
HitaplataHitaplata
Hlífðargleraugu gegn efnaslettumHlífðargleraugu gegn efnaslettum
GúmmíhanskarGúmmíhanskar
3

Wash, dry and pre-heat at 700 °C

Wash out the deposit, dry it, and pre-heat it at 700 °C so it moulds better.

Nauðsynleg verkfæri:

SíupappírSíupappír
Eimað vatnEimað vatn
ÞurrkofnÞurrkofn
PípuofnPípuofn
Deigla með loki (postulín)Deigla með loki (postulín)
Hitaþolnir hanskarHitaþolnir hanskar
4

Mould a ring at 4 tons per cm²

Mould the powder at 4 tons per square centimetre into a ring 3 cm across with a 4 × 4 mm section.

Nauðsynleg verkfæri:

VökvapressaVökvapressa
HringpressumótHringpressumót
RykgrímaRykgríma
5

Heat 3 hours at 900 °C, cool to 600 °C, hold 30 hours

Heat the ring for about 3 hours at 900 °C, cool it to 600 °C at 5 °C per minute, hold it there for 30 hours and let it cool to room temperature, all in a current of oxygen. Snoek's core: initial permeability 500.

Nauðsynleg verkfæri:

PípuofnPípuofn
SúrefniSúrefni
ÞrýstigaskúturÞrýstigaskútur
HáhitamælirHáhitamælir
DeiglutöngDeiglutöng
Hitaþolnir hanskarHitaþolnir hanskar

Efni

5

Nauðsynleg verkfæri

18

Þessi teikning býr til

Thumbnail
Tímabundinn texti

Ferrít-hringkjarni

Free

254
0
1

Tengd Blueprint

Þessi blueprint deila þekkingu — tækni, efni eða meginreglur

Ferrite Toroid Core: Copper-Zinc Ferrite Milled 200 Hours, Fired at 1050 °C (Snoek)

Ferrite Toroid Core: Copper-Zinc Ferrite Milled 200 Hours, Fired at 1050 °C (Snoek)

eftir CharlieDE

Iðnaður

12
0
0
0
0
0
Ferric Nitrate: Scrap Iron Dissolved in Concentrated Nitric Acid (Thorpe 1912)
Hættulegt

Ferric Nitrate: Scrap Iron Dissolved in Concentrated Nitric Acid (Thorpe 1912)

eftir CharlieDE

Iðnaður

8
0
0
0
0
0

CC0 opinbert ríki

Þessi teikning er gefin út undir CC0. Þér er frjálst að afrita, breyta, dreifa og nota þetta verk í hvaða tilgangi sem er, án þess að biðja um leyfi.

Studdu smiðinn með því að kaupa vörur í gegnum teikningu hans þar sem hann fær þóknun smiða sem seljendur ákvarða, eða búðu til nýja endurskoðun á þessari teikningu og tengdu hana sem tengingu í þinni eigin teikningu til að deila tekjum.

Umræða

(0)

Skrá inn til að taka þátt í umræðunni

Hleður athugasemdum...