Ferrite Toroid Core: Magnesium-Zinc Ferrite (28 : 18 : 54) Fired at 1400 °C (Snoek)
Charlie

Búin til af

Charlie

21. október 2026DE
3
0
0
0
0

Ferrite Toroid Core: Magnesium-Zinc Ferrite (28 : 18 : 54) Fired at 1400 °C (Snoek)

Ferrite is a ceramic magnet: iron oxide combined with other metal oxides, carrying magnetic flux while hardly conducting electricity. In his first ferrite patent (US 2,452,529, 1948) Snoek at Philips ground the oxides very fine and fired rings in oxygen. This magnesium-zinc ferrite (28 : 18 : 54 mol %) is milled 30 hours and fired 2 hours at 1400 °C; his core had an initial permeability of 150. The picture: our diagram.
Lengra kominn
3 days

Leiðbeiningar

1

Mix 28 : 18 : 54 mol

Mix pure magnesium oxide, zinc oxide and ferric oxide, 28 : 18 : 54 mol %. Ours, by weight: 10.06 g magnesium oxide, 13.06 g zinc oxide and 76.88 g ferric oxide per 100 g.

Efni fyrir þetta skref:

MagnesíumoxíðMagnesíumoxíð10.06 g
SinkoxíðduftSinkoxíðduft13.06 g
Járn(III)oxíðJárn(III)oxíð76.88 g

Nauðsynleg verkfæri:

SkálavogSkálavog
RykgrímaRykgríma
2

Grind 30 hours in an iron ball mill

Grind the mixture for 30 hours in an iron ball mill.

Nauðsynleg verkfæri:

JárnkúlukvörnJárnkúlukvörn
RykgrímaRykgríma
3

Mould a ring at 4 tons per cm²

Press the powder at 4 tons per square centimetre into a ring 3 cm across with a 4 × 4 mm section.

Nauðsynleg verkfæri:

VökvapressaVökvapressa
HringpressumótHringpressumót
4

Fire 2 hours at 1400 °C, cool slowly

Heat the ring in oxygen for 2 hours at 1400 °C, then cool it slowly in oxygen at 5–10 °C a minute. Snoek's core: initial permeability 150.

Nauðsynleg verkfæri:

PípuofnPípuofn
SúrefniSúrefni
ÞrýstigaskúturÞrýstigaskútur
HáhitamælirHáhitamælir
DeiglutöngDeiglutöng
Hitaþolnir hanskarHitaþolnir hanskar

Efni

3

Nauðsynleg verkfæri

11

Þessi teikning býr til

Thumbnail
Tímabundinn texti

Ferrít-hringkjarni

Free

249
0
1

Tengd Blueprint

Þessi blueprint deila þekkingu — tækni, efni eða meginreglur

Ferrite Toroid Core: Nickel-Zinc Ferrite Sintered at 1300 °C in Oxygen (Snoek)
Hættulegt

Ferrite Toroid Core: Nickel-Zinc Ferrite Sintered at 1300 °C in Oxygen (Snoek)

eftir CharlieDE

Iðnaður

5
0
0
0
0
0
Ferric Oxide: Hydroxide Precipitated from Ferric Chloride with Ammonia, Then Heated

Ferric Oxide: Hydroxide Precipitated from Ferric Chloride with Ammonia, Then Heated

eftir CharlieDE

Ólífrænt

3
0
0
0
0
0

CC0 opinbert ríki

Þessi teikning er gefin út undir CC0. Þér er frjálst að afrita, breyta, dreifa og nota þetta verk í hvaða tilgangi sem er, án þess að biðja um leyfi.