Lead Ferrite Disc Magnet: 0.3 mol PbO2 to 1.2 mol Iron Oxide, Two-Stage Presinter (Went, Philips 1956, Ex. 15)
A ceramic magnet with lead in place of barium: 0.3 mol lead dioxide to 1.2 mol iron oxide, milled, pressed into pastilles, presintered at 700 °C and 900 °C, ground in a mortar, pressed and passed through a 1150 °C furnace in 3 to 5 minutes. Went's rod held 1,630 gauss with a coercive force of 1,000 oersted. Lead compounds are poisonous.
Source: J. J. Went, G. W. van Oosterhout and E. W. Gorter (Philips), US 2,762,777 (1956), Example 15. They sintered rods; discs and the magnetising are ours. Picture: ferrite magnets, Omegatron, Wikimedia Commons, CC BY-SA 3.0.
Lengra kominn
2 days
Hættulegt efni
Þessi teikning inniheldur hættulegar aðferðir. Skráðu þig inn og virkjaðu hættulegt efni í stillingum reikningsins til að sjá skref-fyrir-skref leiðbeiningar.
Skrá innÞessi teikning býr til
Tengd Blueprint
Þessi blueprint deila þekkingu — tækni, efni eða meginreglur
CC0 opinbert ríki
Þessi teikning er gefin út undir CC0. Þér er frjálst að afrita, breyta, dreifa og nota þetta verk í hvaða tilgangi sem er, án þess að biðja um leyfi.
Studdu smiðinn með því að kaupa vörur í gegnum teikningu hans þar sem hann fær þóknun smiða sem seljendur ákvarða, eða búðu til nýja endurskoðun á þessari teikningu og tengdu hana sem tengingu í þinni eigin teikningu til að deila tekjum.