Neodymium Magnets: Melt-Spun Ribbon Milled, Pressed in a Field, Sintered and Magnetised at 30 kOe (Sato, Tokin, US 4,881,986)
Squirting the molten Nd-Fe-B alloy onto a spinning copper wheel freezes it into ribbon with crystals only a tenth of a micron across. Milled fine, lined up in a magnetic field, pressed and sintered, it makes a strong anisotropic magnet, which a 30 kOe pulse then magnetises.
Result: sintered neodymium magnets, above 16 MGOe when the powder is finer than 15 microns.
Source: Sato and Tachiya, US 4,881,986 (Tokin, 1989), Example 1. Not given: magnet shape and size. Picture drawn by Youblob.
Lengra kominn
3 days
Leiðbeiningar
1
1
Melt the alloy in argon
Melt the alloy in argon
Weigh 35.0 % neodymium, 0.9 % boron (as ferroboron with 20 % B) and the rest electrolytic iron, by weight, and induction-melt them in argon into an ingot. Ours, worked out: 35 parts neodymium, 4.5 ferroboron, 60.5 iron. Sato's neodymium was 97 % (with Ce and Pr); ours is the 99 % metal.
Efni fyrir þetta skref:
Neódýmmálmur35 parts
Járnbór4.5 parts
Rafgreint járn60.5 partsNauðsynleg verkfæri:
Skálavog
Spanofn
Þrýstigaskútur2
2
Melt-spin a ribbon
Melt-spin a ribbon
Remelt in argon and squirt the alloy through a small orifice onto a copper wheel whose rim moves at 15 m/s. It freezes into ribbon about 5 mm wide and 100 microns thick, with R2Fe14B grains about 0.1 micron.
Nauðsynleg verkfæri:
Spanofn
BræðslusnúðurÞrýstigaskútur3
3
Ball-mill to powder
Ball-mill to powder
Crush and ball-mill the ribbon. Particle size: Sato made 0.5 to 30 microns; below 15 microns the magnet tops 16 MGOe, better below 10, best at 5 microns or less.
Nauðsynleg verkfæri:
Járnkúlukvörn4
4
Press in a 20 kOe field and sinter
Press in a 20 kOe field and sinter
Press the powder at 1 ton/cm² in a 20 kOe field. Sinter at 1,050 °C for 1 hour in vacuum and 1 more hour in argon, then quench; age at 630 °C for 1 hour in argon.
Nauðsynleg verkfæri:
Segulsviðspressa
Pípuofn
LofttæmidælaÞrýstigaskútur5
5
Magnetise at 30 kOe
Magnetise at 30 kOe
Magnetise the sintered body in a field of about 30 kOe.
Nauðsynleg verkfæri:
SegulmagnariEfni
3- 35 partsStaðgengill
- 4.5 partsStaðgengill
- 60.5 partsStaðgengill
Nauðsynleg verkfæri
9- Staðgengill
- Staðgengill
- Staðgengill
- Staðgengill
- Staðgengill
- Staðgengill
- Staðgengill
- Lofttæmidæla10% þóknunMagento Legacy Storeships internationallyStaðgengill
- Staðgengill
Þessi teikning býr til
Tengd Blueprint
Þessi blueprint deila þekkingu — tækni, efni eða meginreglur
CC0 opinbert ríki
Þessi teikning er gefin út undir CC0. Þér er frjálst að afrita, breyta, dreifa og nota þetta verk í hvaða tilgangi sem er, án þess að biðja um leyfi.
Studdu smiðinn með því að kaupa vörur í gegnum teikningu hans þar sem hann fær þóknun smiða sem seljendur ákvarða, eða búðu til nýja endurskoðun á þessari teikningu og tengdu hana sem tengingu í þinni eigin teikningu til að deila tekjum.