Strontium Ferrite Disc Magnet: 0.8 mol SrCO3 to 3.2 mol Iron Oxide, 1280 °C (Went, Philips 1956, Ex. 11)
Omegatron (Wikimedia Commons) · CC BY-SA 3.0
Charlie

Búin til af

Charlie

28. október 2026DE
2
0
0
0
0

Strontium Ferrite Disc Magnet: 0.8 mol SrCO3 to 3.2 mol Iron Oxide, 1280 °C (Went, Philips 1956, Ex. 11)

A strontium ferrite: 0.8 mol strontium carbonate to 3.2 mol iron oxide, milled, bound and formed as in Example 4, and passed through a 1280 °C furnace in 10 minutes. Went's rod held 1,730 gauss with a coercive force of 3,090 oersted. Source: J. J. Went, G. W. van Oosterhout and E. W. Gorter (Philips), US 2,762,777 (1956), Example 11. They sintered rods; discs and the magnetising are ours. Picture: ferrite magnets, Omegatron, Wikimedia Commons, CC BY-SA 3.0.
Lengra kominn
2 days

Leiðbeiningar

1

Weigh strontium carbonate and iron oxide

Weigh 118.1 g strontium carbonate (0.8 mol) and 510.9 g ferric oxide (3.2 mol).

Efni fyrir þetta skref:

StrontíumkarbónatStrontíumkarbónat118.1 g
Járn(III)oxíðJárn(III)oxíð510.9 g

Nauðsynleg verkfæri:

SkálavogSkálavog
P100-öndunargrímaP100-öndunargríma
2

Mill with alcohol 15.5 hours, dry and sieve

As in Example 4: grind the mixture with alcohol in a ball mill for 15.5 hours, then dry it and sieve it.

Nauðsynleg verkfæri:

JárnkúlukvörnJárnkúlukvörn
Etanól - rannsóknargráða, 95 %Etanól - rannsóknargráða, 95 %
ÞurrkofnÞurrkofn
GrófsigtiGrófsigti
3

Knead with a binder and form

Mix 300 g of the powder with a binder such as polyvinyl alcohol (Went names it or nitrocellulose) into a kneadable mass. The patent extrudes rods about 3 mm across; ours: press discs at 1.5 tonnes per cm², as in its other examples. Dry them in air for about 24 hours.

Nauðsynleg verkfæri:

PólývínýlalkóhólduftPólývínýlalkóhólduft
VökvapressaVökvapressa
Pressumót fyrir skífurPressumót fyrir skífur
ÞurrkofnÞurrkofn
4

Pass through a 1280 °C zone in 10 minutes

Sinter in air at 1280 °C by passing the pieces through a 10 cm hot zone at 10 mm per minute: 10 minutes in the heat.

Nauðsynleg verkfæri:

PípuofnPípuofn
Hitaþolnir hanskarHitaþolnir hanskar
5

Magnetise the discs

The patent gives no magnetising method. Ours: lay a disc with its faces against the poles of a strong electromagnet, switch the current on, then off. Find which face is north with a compass.

Nauðsynleg verkfæri:

RafmagnssegullRafmagnssegull
ÁttavitiÁttaviti

Efni

2

Nauðsynleg verkfæri

13

Þessi teikning býr til

Thumbnail
Tímabundinn texti

Skífusegull

Free

2
0
1

Tengd Blueprint

Þessi blueprint deila þekkingu — tækni, efni eða meginreglur

Barium Ferrite Disc Magnet: Barium Carbonate and Iron Oxide Sintered (Went, Philips 1956)

Barium Ferrite Disc Magnet: Barium Carbonate and Iron Oxide Sintered (Went, Philips 1956)

eftir CharlieDE

Iðnaður

2
0
0
0
0
0
Strontium Carbonate: Powdered Celestine Boiled with Soda Solution (Thorpe 1912)

Strontium Carbonate: Powdered Celestine Boiled with Soda Solution (Thorpe 1912)

eftir CharlieDE

Iðnaður

6
0
0
0
0
0

CC0 opinbert ríki

Þessi teikning er gefin út undir CC0. Þér er frjálst að afrita, breyta, dreifa og nota þetta verk í hvaða tilgangi sem er, án þess að biðja um leyfi.

Studdu smiðinn með því að kaupa vörur í gegnum teikningu hans þar sem hann fær þóknun smiða sem seljendur ákvarða, eða búðu til nýja endurskoðun á þessari teikningu og tengdu hana sem tengingu í þinni eigin teikningu til að deila tekjum.

Umræða

(0)

Skrá inn til að taka þátt í umræðunni

Hleður athugasemdum...