Strontium Ferrite Disc Magnet: Presintered at 1100 °C, 0.2 mol SrCO3 to 1.1 mol Iron Oxide (Went, Philips 1956, Ex. 7)
Omegatron (Wikimedia Commons) · CC BY-SA 3.0
Charlie

Búin til af

Charlie

28. október 2026DE
2
0
0
0
0

Strontium Ferrite Disc Magnet: Presintered at 1100 °C, 0.2 mol SrCO3 to 1.1 mol Iron Oxide (Went, Philips 1956, Ex. 7)

A strontium ferrite: 0.2 mol strontium carbonate to 1.1 mol iron oxide, dried, milled, presintered 3.5 hours at 1100 °C, bound, formed and passed through a 1280 °C furnace in 10 minutes. Went's rod held 2,155 gauss with a coercive force of 2,500 oersted. Source: J. J. Went, G. W. van Oosterhout and E. W. Gorter (Philips), US 2,762,777 (1956), Example 7. They sintered rods; discs and the magnetising are ours. Picture: ferrite magnets, Omegatron, Wikimedia Commons, CC BY-SA 3.0.
Lengra kominn
2 days

Leiðbeiningar

1

Weigh strontium carbonate and iron oxide

Weigh 29.5 g strontium carbonate (0.2 mol) and 176.1 g ferric oxide (1.1 mol).

Efni fyrir þetta skref:

StrontíumkarbónatStrontíumkarbónat29.5 g
Járn(III)oxíðJárn(III)oxíð176.1 g

Nauðsynleg verkfæri:

SkálavogSkálavog
P100-öndunargrímaP100-öndunargríma
2

Dry at 200 °C, mill with alcohol 4 hours

Dry the mixture at 200 °C, then grind it with alcohol in a ball mill for 4 hours and dry it.

Nauðsynleg verkfæri:

ÞurrkofnÞurrkofn
JárnkúlukvörnJárnkúlukvörn
Etanól - rannsóknargráða, 95 %Etanól - rannsóknargráða, 95 %
3

Presinter in air at 1100 °C for 3.5 hours

Fire the powder in air at 1100 °C for about 3.5 hours.

Nauðsynleg verkfæri:

MúffluofnMúffluofn
Deigla með loki (postulín)Deigla með loki (postulín)
DeiglutöngDeiglutöng
Hitaþolnir hanskarHitaþolnir hanskar
4

Add a binder and form, dry overnight

Add a binder as in Example 1 (polyvinyl alcohol or nitrocellulose). The patent extrudes rods; ours: press discs at 1.5 tonnes per cm². Dry overnight.

Nauðsynleg verkfæri:

PólývínýlalkóhólduftPólývínýlalkóhólduft
VökvapressaVökvapressa
Pressumót fyrir skífurPressumót fyrir skífur
ÞurrkofnÞurrkofn
5

Pass through a 1280 °C zone in 10 minutes

Sinter in air at 1280 °C by passing the pieces through a 10 cm hot zone at 10 mm per minute: 10 minutes in the heat.

Nauðsynleg verkfæri:

PípuofnPípuofn
Hitaþolnir hanskarHitaþolnir hanskar
6

Magnetise the discs

The patent gives no magnetising method. Ours: lay a disc with its faces against the poles of a strong electromagnet, switch the current on, then off. Find which face is north with a compass.

Nauðsynleg verkfæri:

RafmagnssegullRafmagnssegull
ÁttavitiÁttaviti

Efni

2

Nauðsynleg verkfæri

15

Þessi teikning býr til

Thumbnail
Tímabundinn texti

Skífusegull

Free

2
0
1

Tengd Blueprint

Þessi blueprint deila þekkingu — tækni, efni eða meginreglur

Barium Ferrite Disc Magnet: Barium Carbonate and Iron Oxide Sintered (Went, Philips 1956)

Barium Ferrite Disc Magnet: Barium Carbonate and Iron Oxide Sintered (Went, Philips 1956)

eftir CharlieDE

Iðnaður

2
0
0
0
0
0
Strontium Carbonate: Powdered Celestine Boiled with Soda Solution (Thorpe 1912)

Strontium Carbonate: Powdered Celestine Boiled with Soda Solution (Thorpe 1912)

eftir CharlieDE

Iðnaður

6
0
0
0
0
0

CC0 opinbert ríki

Þessi teikning er gefin út undir CC0. Þér er frjálst að afrita, breyta, dreifa og nota þetta verk í hvaða tilgangi sem er, án þess að biðja um leyfi.

Studdu smiðinn með því að kaupa vörur í gegnum teikningu hans þar sem hann fær þóknun smiða sem seljendur ákvarða, eða búðu til nýja endurskoðun á þessari teikningu og tengdu hana sem tengingu í þinni eigin teikningu til að deila tekjum.

Umræða

(0)

Skrá inn til að taka þátt í umræðunni

Hleður athugasemdum...