Metal Oxide Varistor: Zinc Oxide with Manganese and Titanium Oxides, Bismuth Paste Fired On (Masuyama 1972, Ex. 6)
A varistor with manganese dioxide and titanium dioxide mixed into the zinc oxide, and bismuth oxide fired on from a paste: 99.0 % zinc oxide, 0.5 % manganese dioxide and 0.5 % titanium dioxide by moles, sintered at 1350 °C, coated with bismuth oxide paste and fired at 800 °C. The disc measured a C-value of 66 at 1 mA and a nonlinearity exponent n of 13.7.
Source: T. Masuyama, M. Matsuoka and T. Nishi (Matsushita), US 3,663,458 (1972), Example 6. Unknown: what the silver paint is, and how strong the epoxy solution of the paste is. The spraying is ours, after US Army Corps of Engineers EM 1110-2-3401 (1999). The 10 g batch is our arithmetic. Picture: the patent's drawing.
Lengra kominn
2 days
Leiðbeiningar
1
1
Weigh 99 : 0.5 : 0.5 and wet-mill 5 hours
Weigh 99 : 0.5 : 0.5 and wet-mill 5 hours
Mix zinc oxide, manganese dioxide and titanium dioxide 99 : 0.5 : 0.5 by moles. Ours, for 10 g: 9.898 g zinc oxide, 0.053 g manganese dioxide, 0.049 g titanium dioxide (our arithmetic). Mill wet for 5 hours, then dry, as in Example 1. Unknown: the milling liquid.
Efni fyrir þetta skref:
Sinkoxíðduft9.898 g
Mangandíoxíð (pýrólúsít)0.053 g
Títantvíoxíð0.049 gNauðsynleg verkfæri:
Skálavog
Járnkúlukvörn
Þurrkofn2
2
Press discs 13 mm by 2.5 mm
Press discs 13 mm by 2.5 mm
Press discs 13 mm across and 2.5 mm thick at 340 kg/cm², as in Example 1.
Nauðsynleg verkfæri:
Vökvapressa
Pressumót fyrir skífur
Skífmælir3
3
Sinter 1 hour at 1350 °C and furnace-cool
Sinter 1 hour at 1350 °C and furnace-cool
Sinter in air at 1350 °C for 1 hour and let the discs cool in the furnace.
Nauðsynleg verkfæri:
Múffluofn4
4
Lap both faces
Lap both faces
Lap both faces with silicon carbide abrasive. Example 6 gives no thickness.
Nauðsynleg verkfæri:
KísilkarbíðkornSkífmælir5
5
Coat with bismuth oxide paste and fire at 800 °C
Coat with bismuth oxide paste and fire at 800 °C
Coat both lapped faces with a paste of 50 % by weight bismuth oxide in a solution of epoxy resin in butyl alcohol, and fire it in air at 800 °C for 30 minutes. The bismuth oxide diffuses into the zinc oxide. Not given: how much paste, or the strength of the epoxy solution.
Efni fyrir þetta skref:
Bismútoxíð1 as requiredNauðsynleg verkfæri:
Epoxýkvoða
n-BútanólMúffluofn6
6
Spray aluminium electrodes and attach leads
Spray aluminium electrodes and attach leads
Spray a metallised film of aluminium on both faces. Attach a lead wire to each with conductive silver paint, as in Example 1. Ours, after US Army Corps of Engineers EM 1110-2-3401 (1999): wire-arc spray the aluminium from two 3.2 mm wires melted by an 18-40 V DC arc and atomised by compressed air, 15-20 cm from the disc and never at less than 45°, in at least two coats at right angles of 50-75 µm each. Unknown: the paint.
Efni fyrir þetta skref:
Álhleifur1 as 3.2 mm spray wire
Leiðandi silfurmálning1 as required
Koparvír2 stykkiNauðsynleg verkfæri:
Skífmælir
Ljósbogaúðabyssa
IðnaðarloftþjappaEfni
7- 9.898 gStaðgengill
- 0.053 gStaðgengill
- 0.049 gStaðgengill
- 1 as requiredStaðgengill
- 1 as 3.2 mm spray wireStaðgengill
- 1 as requiredStaðgengill
- 2 stykkiStaðgengill
Nauðsynleg verkfæri
12- Staðgengill
- Staðgengill
- Staðgengill
- Staðgengill
- Staðgengill
- Staðgengill
- Staðgengill
- Staðgengill
- Staðgengill
- Staðgengill
- Staðgengill
- Staðgengill
Þessi teikning býr til
Tengd Blueprint
Þessi blueprint deila þekkingu — tækni, efni eða meginreglur
CC0 opinbert ríki
Þessi teikning er gefin út undir CC0. Þér er frjálst að afrita, breyta, dreifa og nota þetta verk í hvaða tilgangi sem er, án þess að biðja um leyfi.
Studdu smiðinn með því að kaupa vörur í gegnum teikningu hans þar sem hann fær þóknun smiða sem seljendur ákvarða, eða búðu til nýja endurskoðun á þessari teikningu og tengdu hana sem tengingu í þinni eigin teikningu til að deila tekjum.