Barium-Calcium Ferrite Disc Magnet: Part of the Barium Replaced by Calcium (Went, Philips 1956, Ex. 21)
A ceramic magnet in which part of the barium is replaced by calcium: 0.06 mol barium carbonate and 0.04 mol calcium carbonate to 0.6 mol iron oxide, milled, fired in oxygen, milled again, pressed and passed quickly through a hot furnace. Went's rod held 1,660 gauss with a coercive force of 1,210 oersted.
Source: J. J. Went, G. W. van Oosterhout and E. W. Gorter (Philips), US 2,762,777 (1956), Example 21. They sintered rods; discs and the magnetising are ours. Picture: ferrite magnets, Omegatron, Wikimedia Commons, CC BY-SA 3.0.
Avanzato
2 days
Istruzioni
1
1
Weigh barium carbonate, chalk and iron oxide
Weigh barium carbonate, chalk and iron oxide
Weigh 11.84 g barium carbonate (0.06 mol), 4.004 g calcium carbonate (0.04 mol) and 99.55 g ferric oxide (0.6 mol). Barium carbonate is poisonous if swallowed: gloves and a dust respirator.
Materiali per questo passaggio:
Carbonato di bario (witherite)11.84 g
Carbonato di calcio (bianco di Spagna)4.004 g
Ossido ferrico99.55 gStrumenti necessari:
Bilancia a bracci
Guanti di gomma
Respiratore P1002
2
Mill with alcohol 4 hours and dry
Mill with alcohol 4 hours and dry
Grind the mixture with alcohol in a ball mill for 4 hours, then dry it.
Strumenti necessari:
Mulino a sfere di ferro
Etanolo per laboratorio, 95 %
Essiccatoio3
3
Presinter in oxygen at 1000 °C for 2 hours
Presinter in oxygen at 1000 °C for 2 hours
Fire the dry powder in oxygen at 1000 °C for 2 hours (ours: a tube furnace fed from an oxygen cylinder).
Strumenti necessari:
Forno a tubo
Ossigeno
Bombola di gas in pressione
Guanti resistenti al calore4
4
Mill again 4 hours, dry, press at 1.5 t/cm²
Mill again 4 hours, dry, press at 1.5 t/cm²
Grind with alcohol in the ball mill for 4 hours, dry, and press at 1.5 tonnes per cm² (ours: discs instead of rods).
Strumenti necessari:
Mulino a sfere di ferroEtanolo per laboratorio, 95 %Essiccatoio
Pressa idraulica
Stampo per pressatura di dischi5
5
Pass through a 1200 °C zone in 10 minutes
Pass through a 1200 °C zone in 10 minutes
Sinter at 1200 °C by passing the pieces through a 10 cm hot zone at 10 mm per minute, which is 10 minutes in the heat.
Strumenti necessari:
Forno a tuboGuanti resistenti al calore6
6
Magnetise the discs
Magnetise the discs
The patent gives no magnetising method. Ours: lay a disc with its faces against the poles of a strong electromagnet, switch the current on, then off. Find which face is north with a compass.
Strumenti necessari:
Elettromagnete
BussolaMateriali
3- Segnaposto
- Segnaposto
- 99.55 gSegnaposto
Strumenti richiesti
14- Segnaposto
- Segnaposto
- Segnaposto
- Segnaposto
- Segnaposto
- Segnaposto
- Segnaposto
- Segnaposto
- Segnaposto
- Segnaposto
- Segnaposto
- Segnaposto
- Segnaposto
- Segnaposto
Questo progetto realizza
Blueprint correlati
Questi blueprint condividono conoscenze — tecniche, materiali o principi
CC0 Pubblico dominio
Questo progetto è rilasciato sotto CC0. Sei libero di copiare, modificare, distribuire e utilizzare quest'opera per qualsiasi scopo, senza chiedere permesso.
Supporta il Maker acquistando prodotti tramite il suo progetto dove guadagna una Commissione Maker stabilita dai venditori, oppure crea una nuova iterazione di questo progetto e includilo come collegamento nel tuo progetto per condividere i ricavi.