Ferrite Toroid Core: Copper-Zinc Ferrite Sintered at 1200 °C (Snoek 1948, Ex. I)
A soft ferrite ring core for coils and transformers: copper, zinc and iron oxides with a little brownstone, pressed into a ring and sintered at 1200 °C in oxygen. Snoek's ring had an initial permeability of 285.
Source: J. L. Snoek, US 2,452,530 (Philips, 1948), Example I and its table. The violet iron oxide has its own blueprint (precipitated hematite calcined at 1000-1100 °C, after Nurdini et al. 2022); Snoek does not say how his was made. Picture: the patent's Fig. 4, the ring core.
Avanzato
2 days
Istruzioni
1
1
Weigh 20 : 30 : 50 mol % and 1 % brownstone
Weigh 20 : 30 : 50 mol % and 1 % brownstone
Mix 20 mol % pure copper oxide, 30 mol % pure zinc oxide and 50 mol % pure violet iron oxide, and add 1 % by weight of brownstone (manganese dioxide). Ours, by weight: 13.24 g copper oxide, 20.32 g zinc oxide and 66.44 g iron oxide per 100 g, plus 1 g brownstone. Snoek does not say what makes it 'violet'; violet iron oxide has its own blueprint.
Materiali per questo passaggio:
Ossido di rame13.24 g
Polvere di ossido di zinco20.32 g
Ossido di ferro violetto66.44 g
Biossido di manganese (pirolusite)1 gStrumenti necessari:
Bilancia a bracci
Mascherina antipolvere2
2
Grind half an hour in an iron ball mill
Grind half an hour in an iron ball mill
Grind the mixture for half an hour in a mill with iron balls.
Strumenti necessari:
Mulino a sfere di ferroMascherina antipolvere3
3
Press a ring at 4 tons per cm²
Press a ring at 4 tons per cm²
Press the powder at 4 tons per square centimetre into a ring 3 cm across with a 4 × 4 mm cross-section.
Strumenti necessari:
Pressa idraulica
Stampo di pressatura ad anelloMascherina antipolvere4
4
Sinter at 1200 °C in oxygen, cool 5–10 °C a minute
Sinter at 1200 °C in oxygen, cool 5–10 °C a minute
Sinter the ring at 1200 °C in a current of oxygen. Example I heats for 1 hour and cools in the oxygen at 5 to 10 °C per minute. Snoek's ring had an initial permeability of 285, measured at room temperature at 2 kHz.
Strumenti necessari:
Forno a tubo
Ossigeno
Bombola di gas in pressione
Pirometro
Tenaglia per crogiolo
Guanti resistenti al caloreMateriali
4- 13.24 gSegnaposto
- 20.32 gSegnaposto
- 66.44 gSegnaposto
- Segnaposto
Strumenti richiesti
11- Segnaposto
- Segnaposto
- Segnaposto
- Segnaposto
- Segnaposto
- Segnaposto
- Segnaposto
- Segnaposto
- Segnaposto
- Segnaposto
- Segnaposto
Questo progetto realizza
Blueprint correlati
Questi blueprint condividono conoscenze — tecniche, materiali o principi
CC0 Pubblico dominio
Questo progetto è rilasciato sotto CC0. Sei libero di copiare, modificare, distribuire e utilizzare quest'opera per qualsiasi scopo, senza chiedere permesso.
Supporta il Maker acquistando prodotti tramite il suo progetto dove guadagna una Commissione Maker stabilita dai venditori, oppure crea una nuova iterazione di questo progetto e includilo come collegamento nel tuo progetto per condividere i ricavi.