Strontium-Calcium Ferrite Disc Magnet: Equal Strontium and Calcium, 1280 °C (Went, Philips 1956, Ex. 27)
Omegatron (Wikimedia Commons) · CC BY-SA 3.0
Charlie

Creato da

Charlie

28. ottobre 2026DE
6
0
0
0
0

Strontium-Calcium Ferrite Disc Magnet: Equal Strontium and Calcium, 1280 °C (Went, Philips 1956, Ex. 27)

A ferrite with half the strontium replaced by calcium: 0.3 mol strontium carbonate and 0.3 mol calcium carbonate to 3.1 mol iron oxide, milled 15 hours, pressed and passed through a 1280 °C furnace in 10 minutes. Went's rod held 1,645 gauss with a coercive force of 2,460 oersted. Source: J. J. Went, G. W. van Oosterhout and E. W. Gorter (Philips), US 2,762,777 (1956), Example 27. They sintered rods; discs and the magnetising are ours. Picture: ferrite magnets, Omegatron, Wikimedia Commons, CC BY-SA 3.0.
Avanzato
2 days

Istruzioni

1

Weigh the carbonates and iron oxide

Weigh 44.3 g strontium carbonate (0.3 mol), 30.2 g calcium carbonate (0.3 mol), 500.0 g ferric oxide (3.1 mol).

Materiali per questo passaggio:

Carbonato di stronzioCarbonato di stronzio44.3 g
Carbonato di calcio (bianco di Spagna)Carbonato di calcio (bianco di Spagna)30.2 g
Ossido ferricoOssido ferrico500 g

Strumenti necessari:

Bilancia a bracciBilancia a bracci
Respiratore P100Respiratore P100
2

Mill with alcohol 15 hours, dry

Grind the mixture with alcohol in a ball mill for 15 hours, then dry it.

Strumenti necessari:

Mulino a sfere di ferroMulino a sfere di ferro
Etanolo per laboratorio, 95 %Etanolo per laboratorio, 95 %
EssiccatoioEssiccatoio
3

Press at 1.5 t/cm²

Press the dry powder at 1.5 tonnes per cm² (ours: discs instead of a rod).

Strumenti necessari:

Pressa idraulicaPressa idraulica
Stampo per pressatura di dischiStampo per pressatura di dischi
4

Pass through a 1280 °C zone in 10 minutes

Sinter at 1280 °C by passing the pieces through a 10 cm hot zone at 10 mm per minute: 10 minutes in the heat.

Strumenti necessari:

Forno a tuboForno a tubo
Guanti resistenti al caloreGuanti resistenti al calore
5

Magnetise the discs

The patent gives no magnetising method. Ours: lay a disc with its faces against the poles of a strong electromagnet, switch the current on, then off. Find which face is north with a compass.

Strumenti necessari:

ElettromagneteElettromagnete
BussolaBussola

Materiali

3

Strumenti richiesti

11

Questo progetto realizza

Thumbnail
Segnaposto

Magnete a disco

Free

10
0
1

Blueprint correlati

Questi blueprint condividono conoscenze — tecniche, materiali o principi

Barium Ferrite Disc Magnet: Barium Carbonate and Iron Oxide Sintered (Went, Philips 1956)

Barium Ferrite Disc Magnet: Barium Carbonate and Iron Oxide Sintered (Went, Philips 1956)

di CharlieDE

Materiali

9
0
0
0
0
0
Strontium Carbonate: Powdered Celestine Boiled with Soda Solution (Thorpe 1912)

Strontium Carbonate: Powdered Celestine Boiled with Soda Solution (Thorpe 1912)

di CharlieDE

Organico

14
0
0
0
0
0

CC0 Pubblico dominio

Questo progetto è rilasciato sotto CC0. Sei libero di copiare, modificare, distribuire e utilizzare quest'opera per qualsiasi scopo, senza chiedere permesso.

Supporta il Maker acquistando prodotti tramite il suo progetto dove guadagna una Commissione Maker stabilita dai venditori, oppure crea una nuova iterazione di questo progetto e includilo come collegamento nel tuo progetto per condividere i ricavi.

Commenti

(0)

Accedi per partecipare alla discussione

Caricamento commenti...