Strontium Ferrite Disc Magnet: 0.4 mol SrCO3 to 3.6 mol Iron Oxide, 1270 °C (Went, Philips 1956, Ex. 14)
A ceramic magnet with strontium in place of barium: 0.4 mol strontium carbonate to 3.6 mol iron oxide, milled 15 hours and passed through a 1270 °C furnace in 20 minutes. Went's rod held 1,290 gauss with a coercive force of 3,080 oersted.
Source: J. J. Went, G. W. van Oosterhout and E. W. Gorter (Philips), US 2,762,777 (1956), Example 14. They sintered rods; discs and the magnetising are ours. Picture: ferrite magnets, Omegatron, Wikimedia Commons, CC BY-SA 3.0.
Avanzato
2 days
Istruzioni
1
1
Weigh strontium carbonate and iron oxide
Weigh strontium carbonate and iron oxide
Weigh 59.1 g strontium carbonate (0.4 mol) and 580.0 g ferric oxide (3.6 mol).
Materiali per questo passaggio:
Carbonato di stronzio59.1 g
Ossido ferrico580 gStrumenti necessari:
Bilancia a bracci
Respiratore P1002
2
Mill with alcohol 15 hours and dry
Mill with alcohol 15 hours and dry
Grind with alcohol in a ball mill for 15 hours and dry.
Strumenti necessari:
Mulino a sfere di ferro
Etanolo per laboratorio, 95 %
Essiccatoio3
3
Form the pieces and dry overnight
Form the pieces and dry overnight
The patent extrudes rods; ours: press discs at 1.5 tonnes per cm², as in its other examples. Dry overnight.
Strumenti necessari:
Pressa idraulica
Stampo per pressatura di dischiEssiccatoio4
4
Pass through a 1270 °C zone in 20 minutes
Pass through a 1270 °C zone in 20 minutes
Sinter in air at 1270 °C by passing the pieces through a 10 cm hot zone at 5 mm per minute: 20 minutes in the heat.
Strumenti necessari:
Forno a tubo
Guanti resistenti al calore5
5
Magnetise the discs
Magnetise the discs
The patent gives no magnetising method. Ours: lay a disc with its faces against the poles of a strong electromagnet, switch the current on, then off. Find which face is north with a compass.
Strumenti necessari:
Elettromagnete
BussolaMateriali
2- 59.1 gSegnaposto
- 580 gSegnaposto
Strumenti richiesti
11- Segnaposto
- Segnaposto
- Segnaposto
- Segnaposto
- Segnaposto
- Segnaposto
- Segnaposto
- Segnaposto
- Segnaposto
- Segnaposto
- Segnaposto
Questo progetto realizza
Blueprint correlati
Questi blueprint condividono conoscenze — tecniche, materiali o principi
CC0 Pubblico dominio
Questo progetto è rilasciato sotto CC0. Sei libero di copiare, modificare, distribuire e utilizzare quest'opera per qualsiasi scopo, senza chiedere permesso.
Supporta il Maker acquistando prodotti tramite il suo progetto dove guadagna una Commissione Maker stabilita dai venditori, oppure crea una nuova iterazione di questo progetto e includilo come collegamento nel tuo progetto per condividere i ricavi.