Strontium Ferrite Disc Magnet: Presintered, 4 Minutes at 1150 °C (Went, Philips 1956, Ex. 25)
Omegatron (Wikimedia Commons) · CC BY-SA 3.0
Charlie

Creato da

Charlie

28. ottobre 2026DE
1
0
0
0
0

Strontium Ferrite Disc Magnet: Presintered, 4 Minutes at 1150 °C (Went, Philips 1956, Ex. 25)

A strontium ferrite with more strontium: 0.4 mol strontium carbonate to 0.8 mol iron oxide, milled, presintered at 1000 °C, milled again, pressed and passed through a 1150 °C furnace in 4 minutes. Went's rod held 1,200 gauss with a coercive force of 3,710 oersted. Source: J. J. Went, G. W. van Oosterhout and E. W. Gorter (Philips), US 2,762,777 (1956), Example 25. They sintered rods; discs and the magnetising are ours. Picture: ferrite magnets, Omegatron, Wikimedia Commons, CC BY-SA 3.0.
Avanzato
2 days

Istruzioni

1

Dry the strontium carbonate and weigh

Dry the strontium carbonate at 100 °C. Weigh 59.05 g of it (0.4 mol) and 127.5 g ferric oxide (0.8 mol).

Materiali per questo passaggio:

Carbonato di stronzioCarbonato di stronzio59.05 g
Ossido ferricoOssido ferrico127.5 g

Strumenti necessari:

EssiccatoioEssiccatoio
Bilancia a bracciBilancia a bracci
Respiratore P100Respiratore P100
2

Mill 7 hours, dry at 110 °C

Grind with alcohol in a ball mill for 7 hours and dry at 110 °C.

Strumenti necessari:

Mulino a sfere di ferroMulino a sfere di ferro
Etanolo per laboratorio, 95 %Etanolo per laboratorio, 95 %
EssiccatoioEssiccatoio
3

Presinter in air at 1000 °C for 4 hours

Fire in air at 1000 °C for 4 hours.

Strumenti necessari:

Forno a muffolaForno a muffola
Crogiolo con coperchio (porcellana)Crogiolo con coperchio (porcellana)
Tenaglia per crogioloTenaglia per crogiolo
Guanti resistenti al caloreGuanti resistenti al calore
4

Mill again, dry, press at 1.5 t/cm²

Grind again 7 hours with alcohol, dry at 110 °C and press at 1.5 tonnes per cm² (ours: discs).

Strumenti necessari:

Mulino a sfere di ferroMulino a sfere di ferro
Etanolo per laboratorio, 95 %Etanolo per laboratorio, 95 %
EssiccatoioEssiccatoio
Pressa idraulicaPressa idraulica
Stampo per pressatura di dischiStampo per pressatura di dischi
5

Pass through a 1150 °C zone in 4 minutes

Sinter at 1150 °C by passing the pieces through a 4 cm hot zone at 10 mm per minute: 4 minutes in the heat.

Strumenti necessari:

Forno a tuboForno a tubo
Guanti resistenti al caloreGuanti resistenti al calore
6

Magnetise the discs

The patent gives no magnetising method. Ours: lay a disc with its faces against the poles of a strong electromagnet, switch the current on, then off. Find which face is north with a compass.

Strumenti necessari:

ElettromagneteElettromagnete
BussolaBussola

Materiali

2

Strumenti richiesti

14

Questo progetto realizza

Thumbnail
Segnaposto

Magnete a disco

Free

10
0
1

Blueprint correlati

Questi blueprint condividono conoscenze — tecniche, materiali o principi

Barium Ferrite Disc Magnet: Barium Carbonate and Iron Oxide Sintered (Went, Philips 1956)

Barium Ferrite Disc Magnet: Barium Carbonate and Iron Oxide Sintered (Went, Philips 1956)

di CharlieDE

Materiali

9
0
0
0
0
0
Strontium Carbonate: Powdered Celestine Boiled with Soda Solution (Thorpe 1912)

Strontium Carbonate: Powdered Celestine Boiled with Soda Solution (Thorpe 1912)

di CharlieDE

Organico

14
0
0
0
0
0

CC0 Pubblico dominio

Questo progetto è rilasciato sotto CC0. Sei libero di copiare, modificare, distribuire e utilizzare quest'opera per qualsiasi scopo, senza chiedere permesso.

Supporta il Maker acquistando prodotti tramite il suo progetto dove guadagna una Commissione Maker stabilita dai venditori, oppure crea una nuova iterazione di questo progetto e includilo come collegamento nel tuo progetto per condividere i ricavi.

Commenti

(0)

Accedi per partecipare alla discussione

Caricamento commenti...