Barium Ferrite Disc Magnet: Fired in Carbon Dioxide, Pressed at 12 t/cm² (Went, Philips 1956, Ex. 33)
A barium ferrite made with more iron oxide, 0.4 mol barium carbonate to 3.6 mol, fired an hour at 1300 °C in carbon dioxide. Little oxygen gives the hexagonal crystal BaFe18O27, with some iron in the lower state. It is milled again, bound with nitrocellulose or polyvinyl alcohol, and pressed hard at 12 tonnes per cm². Went's rod held 1,260 gauss with a coercive force of 700 oersted.
Source: J. J. Went, G. W. van Oosterhout and E. W. Gorter (Philips), US 2,762,777 (1956), Example 33. They sintered rods; discs and the magnetising are ours. Picture: ferrite magnets, Omegatron, Wikimedia Commons, CC BY-SA 3.0.
上級者
2 days
手順
1
1
Weigh barium carbonate and iron oxide
Weigh barium carbonate and iron oxide
Weigh 79.4 g barium carbonate (0.4 mol) and 580.9 g ferric oxide (3.6 mol). Barium carbonate is poisonous if swallowed: gloves and a dust respirator.
このステップの材料:
炭酸バリウム（毒重石）79.4 g
酸化第二鉄580.9 g必要な工具:
天秤ばかり
ゴム手袋
P100 防じんマスク2
2
Mill 15.5 hours, press a pastille, fire in CO2
Mill 15.5 hours, press a pastille, fire in CO2
Grind with alcohol in a ball mill for 15.5 hours, dry, and press into a pastille. Heat it at 1300 °C in carbon dioxide for 1 hour (ours: a tube furnace fed from a CO2 cylinder).
必要な工具:
鉄製ボールミル
エタノール——試薬級、95 %
乾燥炉
油圧プレス
円板プレス金型
管状炉
二酸化炭素ガス
高圧ガスボンベ
耐熱手袋3
3
Pulverise, mill 14 hours, bind
Pulverise, mill 14 hours, bind
Crush the cooled pastille and grind it with alcohol for 14 hours. Press the powder into a pastille again with a ceramic binder (ours: polyvinyl alcohol, one of the two named), then crush it to grains.
このステップの材料:
ポリビニルアルコール粉末1 as required必要な工具:
鉄製ボールミルエタノール——試薬級、95 %油圧プレス円板プレス金型4
4
Press at 12 tonnes per cm²
Press at 12 tonnes per cm²
Press the grains at 12 tonnes per cm² (ours: discs instead of rods). The patent describes no further firing.
必要な工具:
油圧プレス円板プレス金型5
5
Magnetise the discs
Magnetise the discs
The patent gives no magnetising method. Ours: lay a disc with its faces against the poles of a strong electromagnet, switch the current on, then off. Find which face is north with a compass.
必要な工具:
電磁石
方位磁針材料
3- 79.4 gプレースホルダー
- 580.9 gプレースホルダー
- 1 as requiredプレースホルダー
この設計図で作るもの
関連ブループリント
これらのブループリントは知識を共有しています — 技術、材料、原理
CC0 パブリックドメイン
このブループリントはCC0で公開されています。許可を求めずに、自由にコピー、修正、配布、あらゆる目的で使用できます。
メイカーを応援するには、ブループリント経由で製品を購入してください。メイカーには メイカーコミッション がベンダーにより設定されています。または、このブループリントの新しいイテレーションを作成し、自分のブループリントにコネクションとして含めて収益を共有できます。