Ferrite Toroid Core: Copper-Zinc Ferrite Milled 200 Hours, Fired at 1050 °C (Snoek)
Ferrite is a ceramic magnet: iron oxide combined with other metal oxides, carrying magnetic flux while hardly conducting electricity. In his first ferrite patent (US 2,452,529, 1948) Snoek at Philips ground the oxides very fine and fired rings in oxygen. This copper-zinc ferrite is milled about 200 hours, fired 2 hours at 1050 °C and held 12 hours at 600 °C; his core had an initial permeability of 200.
The picture: our diagram.
上級者
2 weeks
手順
1
1
Mix 20 : 30 : 50 mol
Mix 20 : 30 : 50 mol
Mix pure copper oxide, zinc oxide and ferric oxide, 20 : 30 : 50 mol %. Ours, by weight: 13.24 g copper oxide, 20.32 g zinc oxide and 66.44 g ferric oxide per 100 g.
このステップの材料:
酸化銅13.24 g
酸化亜鉛粉末20.32 g
酸化第二鉄66.44 g必要な工具:
天秤ばかり
防じんマスク2
2
Grind about 200 hours in an iron ball mill
Grind about 200 hours in an iron ball mill
Grind the mixture for about 200 hours in an iron ball mill.
必要な工具:
鉄製ボールミル防じんマスク3
3
Mould a ring at 4 tons per cm²
Mould a ring at 4 tons per cm²
Press the powder at 4 tons per square centimetre into a ring 3 cm across with a 4 × 4 mm section.
必要な工具:
油圧プレス
リング成形ダイス4
4
Fire 2 hours at 1050 °C, hold 12 hours at 600 °C
Fire 2 hours at 1050 °C, hold 12 hours at 600 °C
Heat the ring for two hours at 1050 °C in a current of oxygen, cool at 5 °C a minute to 600 °C, hold it there 12 hours, then cool to room temperature, all in oxygen. Snoek's core: initial permeability 200.
必要な工具:
管状炉
酸素
高圧ガスボンベ
高温計
るつぼばさみ
耐熱手袋この設計図で作るもの
関連ブループリント
これらのブループリントは知識を共有しています — 技術、材料、原理
CC0 パブリックドメイン
このブループリントはCC0で公開されています。許可を求めずに、自由にコピー、修正、配布、あらゆる目的で使用できます。
メイカーを応援するには、ブループリント経由で製品を購入してください。メイカーには メイカーコミッション がベンダーにより設定されています。または、このブループリントの新しいイテレーションを作成し、自分のブループリントにコネクションとして含めて収益を共有できます。