Ferrite Toroid Core: Magnesium-Zinc Ferrite Fired at 1300 °C in Oxygen (Snoek)
Ferrite is a ceramic magnet: iron oxide combined with other metal oxides, carrying magnetic flux while hardly conducting electricity. Snoek at Philips (US 2,452,531, 1948) made this magnesium-zinc ferrite ring: magnesia, zinc oxide and iron oxide ground together, moulded with water into a ring and fired in oxygen at 1300 °C for 1 hour, then cooled slowly. His ring had an initial permeability of 350.
The picture: our diagram.
上級者
1 day
手順
1
1
Mix 26.5 : 26.5 : 47 mol
Mix 26.5 : 26.5 : 47 mol
Mix pure magnesium oxide, zinc oxide and iron oxide in the molecular ratio 26.5 : 26.5 : 47. Ours, by weight: 9.95 g magnesium oxide, 20.10 g zinc oxide and 69.95 g ferric oxide per 100 g.
このステップの材料:
酸化マグネシウム9.95 g
酸化亜鉛粉末20.1 g
酸化第二鉄69.95 g必要な工具:
天秤ばかり
防じんマスク2
2
Grind for 3 hours in an iron ball mill
Grind for 3 hours in an iron ball mill
Grind the mixture for 3 hours in a mill with iron balls.
必要な工具:
鉄製ボールミル防じんマスク3
3
Mould a ring at 4 tons per cm²
Mould a ring at 4 tons per cm²
Mould a ring 3 cm across and 4 × 4 mm in section at 4 tons per square centimetre, with water as the plastifying and binding agent.
必要な工具:
油圧プレス
リング成形ダイス
蒸留水4
4
Fire 1 hour at 1300 °C, cool at 3 °C a minute
Fire 1 hour at 1300 °C, cool at 3 °C a minute
Heat the ring in oxygen to 1300 °C for 1 hour, then cool it in oxygen at about 3 °C per minute. Snoek's ring had an initial permeability of 350.
必要な工具:
管状炉
酸素
高圧ガスボンベ
高温計
るつぼばさみ
耐熱手袋この設計図で作るもの
関連ブループリント
これらのブループリントは知識を共有しています — 技術、材料、原理
CC0 パブリックドメイン
このブループリントはCC0で公開されています。許可を求めずに、自由にコピー、修正、配布、あらゆる目的で使用できます。
メイカーを応援するには、ブループリント経由で製品を購入してください。メイカーには メイカーコミッション がベンダーにより設定されています。または、このブループリントの新しいイテレーションを作成し、自分のブループリントにコネクションとして含めて収益を共有できます。