High-Carbon Steel Wire Rod: Billet Hot-Rolled to 9 mm and Coiled
Wire is drawn from rod, and the rod is rolled hot. In a rod mill a steel billet is heated above its recrystallisation temperature and passed through stand after stand of grooved rolls, each one narrower, until it is a round rod about 9 mm thick. The rod is laid in a coil, ready to be cleaned and drawn into wire.
The picture: our diagram, square billet to round rod to coil.
上級者
Factory process
手順
1
1
Heat the billet
Heat the billet
Heat the high-carbon billet above the steel's recrystallisation temperature.
このステップの材料:
高炭素鋼のビレット1 個必要な工具:
誘導加熱装置2
2
Roll through the stands
Roll through the stands
Pass it through the roughing, intermediate and finishing stands of the rod mill. Each pair of grooved rolls makes the section smaller and rounder, down to about 9 mm.
必要な工具:
圧延機（ローリングミル）3
3
Keep it hot
Keep it hot
Finish about 50–100 °C above the recrystallisation temperature; reheat if the bar cools below it before the last passes.
必要な工具:
誘導加熱装置4
4
Coil the rod
Coil the rod
Lay the hot rod in loops into a coil and let it cool. It comes out covered in mill scale, which is removed before drawing.
5
5
Rod length from one billet
Rod length from one billet
Jupyter ノートブックを読み込み中…
関連ブループリント
これらのブループリントは知識を共有しています — 技術、材料、原理
CC0 パブリックドメイン
このブループリントはCC0で公開されています。許可を求めずに、自由にコピー、修正、配布、あらゆる目的で使用できます。
メイカーを応援するには、ブループリント経由で製品を購入してください。メイカーには メイカーコミッション がベンダーにより設定されています。または、このブループリントの新しいイテレーションを作成し、自分のブループリントにコネクションとして含めて収益を共有できます。