Oriented Barium Ferrite Disc Magnet: Weak 2000 Oersted Field, Then Pressed (Gorter, Philips 1956, Ex. 2)
A ceramic magnet from pre-fired barium ferrite powder suspended in polyvinyl acetate in acetone, oriented in a weak 2000 oersted field, then pressed into a block, heated to 500 °C in a field and sintered at 1300 °C. In the principal direction it held 2,550 gauss with a coercive force of 1,750 oersted and a (BH)max of 1.13 × 10⁶.
Source: E. W. Gorter, G. W. Rathenau and A. L. Stuyts (Philips), US 2,762,778 (1956), Example 2. They made blocks; disc size is ours. Picture: ferrite magnets, Omegatron, Wikimedia Commons, CC BY-SA 3.0.
上級者
3 days
手順
1
1
Weigh barium carbonate and iron oxide
Weigh barium carbonate and iron oxide
Weigh 450 g barium carbonate and 2000 g ferric oxide. Barium carbonate is poisonous if swallowed: gloves and a dust respirator.
このステップの材料:
炭酸バリウム（毒重石）450 g
酸化第二鉄2000 g必要な工具:
天秤ばかり
ゴム手袋
P100 防じんマスク2
2
Mill 20 hours under alcohol, dry
Mill 20 hours under alcohol, dry
Grind the mixture in a ball mill under alcohol for 20 hours, then dry it.
必要な工具:
鉄製ボールミル
エタノール——試薬級、95 %
乾燥炉3
3
Pre-fire: through a 1100 °C zone in 10 minutes
Pre-fire: through a 1100 °C zone in 10 minutes
Pass the dry powder at 20 mm per minute through an electric furnace with a 20 cm hot zone at 1100 °C, in air: 10 minutes in the heat. Let it cool.
必要な工具:
管状炉
蓋付きるつぼ（磁製）
耐熱手袋4
4
Grind 12 hours with alcohol, dry
Grind 12 hours with alcohol, dry
Pulverise the pre-fired material in a ball mill with alcohol for 12 hours, then dry it. This is the pre-fired powder.
必要な工具:
鉄製ボールミルエタノール——試薬級、95 %乾燥炉5
5
Stir into 8 % polyvinyl acetate in acetone
Stir into 8 % polyvinyl acetate in acetone
Dissolve polyvinyl acetate in acetone to a 8 % solution and stir the pre-fired powder into it, 4 cc of solution per 3 g of powder. The binder burns off later.
必要な工具:
ポリ酢酸ビニル
アセトン天秤ばかり6
6
Orient in a 2000 oersted field
Orient in a 2000 oersted field
Put the suspension in a moulding die between the poles of a magnet and apply a first field of 2000 oersted. Switch the field off and remove the binder solution.
必要な工具:
円板プレス金型
電磁石
油圧プレス7
7
Compress into a block
Compress into a block
Compress the powder into a block. The pressure is not given.
必要な工具:
油圧プレス円板プレス金型8
8
Heat to 500 °C in a 2000 oersted field
Heat to 500 °C in a 2000 oersted field
Put the block in an electric furnace between the magnet's poles. With a second field of 2000 oersted along the first field's direction, heat to 500 °C, which burns off the rest of the binder. Then switch the field off.
必要な工具:
管状炉電磁石耐熱手袋9
9
Sinter: through a 1300 °C zone in 5 minutes
Sinter: through a 1300 °C zone in 5 minutes
Pass the block at 20 mm per minute through an electric furnace in air at 1300 °C with a 10 cm hot zone: about 5 minutes in the heat.
必要な工具:
管状炉耐熱手袋10
10
Magnetise in the principal direction
Magnetise in the principal direction
Magnetise the block along the direction of the first field, the principal direction. The patent magnetises it in a field in that direction; ours: an electromagnet. Find the north face with a compass.
必要な工具:
電磁石
方位磁針この設計図で作るもの
関連ブループリント
これらのブループリントは知識を共有しています — 技術、材料、原理
CC0 パブリックドメイン
このブループリントはCC0で公開されています。許可を求めずに、自由にコピー、修正、配布、あらゆる目的で使用できます。
メイカーを応援するには、ブループリント経由で製品を購入してください。メイカーには メイカーコミッション がベンダーにより設定されています。または、このブループリントの新しいイテレーションを作成し、自分のブループリントにコネクションとして含めて収益を共有できます。