PLA Pellets: Purified Lactide Polymerised with a Trace of Litharge
PLA (polylactide) is the polymer of lactic acid, the stock for PLA filament. Schneider's du Pont patent (US 2,703,316, 1955) made a tough, clear polymer by heating very pure lactide with a trace of litharge in a closed, evacuated vessel: at 180 °C it was done in 6½ hours. Above 200 °C the polymer falls back to lactide. Extruding it and cutting the strand into pellets is our step.
The picture: our diagram.
上級者
About 8 hours
手順
1
1
Charge lactide and litharge
Charge lactide and litharge
Weigh 10 parts of purified lactide (melting at 125 °C in the patent's example; it must melt at 120 °C or above) and 0.004 part litharge into the reaction vessel.
このステップの材料:
ラクチド10 parts必要な工具:
酸化鉛（密陀僧）
天秤ばかり
加圧反応器
P100 防じんマスク2
2
Evacuate and close
Evacuate and close
Pump the air out of the vessel and close it.
必要な工具:
真空ポンプ
真空計加圧反応器3
3
Heat 6½ hours at 180 °C
Heat 6½ hours at 180 °C
Heat at 180 °C for 6½ hours. Do not go above 200 °C, where the polymer turns back to lactide. The product is a clear, colourless polymer (the example's softened at about 82 °C).
必要な工具:
乾燥炉
実験用温度計加圧反応器4
4
Extrude and pelletise
Extrude and pelletise
Ours: take the polymer out, melt it through an extruder and cut the cooled strand into pellets.
必要な工具:
プラスチック押出機
ペレタイザー
耐熱手袋この設計図で作るもの
関連ブループリント
これらのブループリントは知識を共有しています — 技術、材料、原理
CC0 パブリックドメイン
このブループリントはCC0で公開されています。許可を求めずに、自由にコピー、修正、配布、あらゆる目的で使用できます。
メイカーを応援するには、ブループリント経由で製品を購入してください。メイカーには メイカーコミッション がベンダーにより設定されています。または、このブループリントの新しいイテレーションを作成し、自分のブループリントにコネクションとして含めて収益を共有できます。